- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 6.4
- 拉伸強度 [MPa]: 34.0
- 彎曲模量 [MPa]: 0.610
- 硬度: 40.0
- 熱變形溫度 [℃]: 119.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 | ||
| Water Absorption | 1.2 % | 1.2 % | 24 hour; ISO Test | ||
| 7.1 % | 7.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 40 | 40 | ASTM Test | ||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ISO 527 | ||
| 34.0 MPa | 4930 psi | 2 in/min; ASTM Test | |||
| 12.0 MPa @Temperature 120 °C | 1740 psi @Temperature 248 °F | ISO Data | |||
| 12.0 MPa @Temperature 120 °C | 1740 psi @Temperature 248 °F | ASTM Test | |||
| 15.0 MPa @Temperature 80.0 °C | 2180 psi @Temperature 176 °F | ASTM Test | |||
| 15.0 MPa @Temperature 80.0 °C | 2180 psi @Temperature 176 °F | ISO Data | |||
| 83.0 MPa @Temperature -40.0 °C | 12000 psi @Temperature -40.0 °F | ASTM Test | |||
| 83.0 MPa @Temperature -40.0 °C | 12000 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ISO 527 | ||
| 30 % | 30 % | 2 in/min; ASTM Test | |||
| 4.0 % @Temperature -40.0 °C | 4.0 % @Temperature -40.0 °F | ISO Data | |||
| 20 % @Temperature 120 °C | 20 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 0.875 GPa | 127 ksi | 1mm/min; ISO 527 | ||
| 0.155 GPa @Temperature 120 °C | 22.5 ksi @Temperature 248 °F | ISO Data | |||
| 0.180 GPa @Temperature 80.0 °C | 26.1 ksi @Temperature 176 °F | ISO Data | |||
| 2.73 GPa @Temperature -40.0 °C | 396 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 28.0 MPa | 4060 psi | ASTM Test | ||
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ASTM Test | ||
| 0.750 GPa | 109 ksi | ISO Data | |||
| Izod Impact, Notched | 6.40 J/cm @Thickness 3.17 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | NB | NB | ISO Test | ||
| 6.00 kJ/m2 @Temperature -40.0 °C | 2.86 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 117 μm/m-°C @Temperature -30.0 - 30.0 °C | 65.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 93.0 μm/m-°C | 51.7 μin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 111 μm/m-°C | 61.7 μin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ISO 75 | ||
| 124 °C | 255 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | ISO 75 | ||
| 47.0 °C | 117 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||