- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.2
- 拉伸強度 [MPa]: 26.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 1.2 % | 1.2 % | 24 hour; ISO Test | ||
| 7.1 % | 7.1 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527 | ||
| 26.0 MPa | 3770 psi | 2 in/min; ASTM Test | |||
| 104 MPa @Temperature -40.0 °C | 15100 psi @Temperature -40.0 °F | ISO Data | |||
| 104 MPa @Temperature -40.0 °C | 15100 psi @Temperature -40.0 °F | ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 30 % | 30 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 0.460 GPa | 66.7 ksi | 1mm/min; ISO 527 | ||
| 0.145 GPa @Temperature 120 °C | 21.0 ksi @Temperature 248 °F | ISO Data | |||
| 0.230 GPa @Temperature 80.0 °C | 33.4 ksi @Temperature 176 °F | ISO Data | |||
| 3.00 GPa @Temperature -40.0 °C | 435 ksi @Temperature -40.0 °F | ISO Data | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||