- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口沖擊強度: 0.48
- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 0.760
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.2 % | 9.2 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Measurement | 220 | 220 | Formic Acid | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50mm/min; ISO 527 | ||
| 46.0 MPa | 6670 psi | 2 in/min; ASTM Test | |||
| 119 MPa @Temperature -40.0 °C | 17300 psi @Temperature -40.0 °F | ISO Data | |||
| 119 MPa @Temperature -40.0 °C | 17300 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Strength | 37.0 MPa | 5370 psi | ASTM Test | ||
| 176 MPa @Temperature -40.0 °C | 25500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.760 GPa | 110 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Blow Molding | ||||
| Processing | Blow molding | ||||
| Injection Molding | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||