- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.5
- 缺口沖擊強度: 0.8
- 拉伸強度 [MPa]: 48.0
- 彎曲模量 [MPa]: 1.04
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 60 | 60 | Formic Acid | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 | ||
| 48.0 MPa | 6960 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| 60 % | 60 % | 2 in/min; ASTM Test | |||
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM Test | ||
| 15.0 MPa @Temperature 120 °C | 2180 psi @Temperature 248 °F | ASTM Test | |||
| 15.0 MPa @Temperature 93.0 °C | 2180 psi @Temperature 199 °F | ASTM Test | |||
| 20.0 MPa @Temperature 65.0 °C | 2900 psi @Temperature 149 °F | ASTM Test | |||
| 175 MPa @Temperature -40.0 °C | 25400 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 1.04 GPa | 151 ksi | ASTM Test | ||
| 0.225 GPa @Temperature 120 °C | 32.6 ksi @Temperature 248 °F | ASTM Test | |||
| 0.240 GPa @Temperature 93.0 °C | 34.8 ksi @Temperature 199 °F | ASTM Test | |||
| 0.320 GPa @Temperature 65.0 °C | 46.4 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM Test | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Rotomolding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||