- 吸水率 [%]: 0.6
- 缺口沖擊強度: 0.32
- 斷裂伸長率 [%]: 117
- 彎曲模量 [MPa]: 3.45
- 硬度: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 7.0 % | 7.0 % | Immersion; ASTM D570(2) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Hardness, Shore D | 85 | 85 | ASTM D2240 |
| Tensile Strength | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Compressive Strength | 96.5 MPa | 14000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 2.21 GPa | 320 ksi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | Dry vs. Steel; QTM 55007 |
| K (wear) Factor | 806 x 10-8 mm3/N-M | 400 x 10-10 in3-min/ft-lb-hr | QTM 55007 |
| Limiting Pressure Velocity | 0.175 MPa-m/sec | 5000 psi-ft/min | 4:1 safety factor applied; QTM 55007 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | EOS/ESD S11.11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 μm/m-°C @Temperature -40.0 - 149 °C | 50.0 μin/in-°F @Temperature -40.0 - 300 °F | ASTM E831 |
| Melting Point | 216 °C | 420 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/8 inch (Estimated Rating) |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |
| USP Class VI | No | No | |
| Chemical Resistance Properties | Metric | English | Comments |
| Acids, Strong (pH 1-3) | Unacceptable | Unacceptable | |
| Acids, Weak | Limited | Limited | |
| Alcohols | Limited | Limited | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Limited | Limited | |
| Chlorinated Solvents | Limited | Limited | |
| Conductive / Static Dissipative | No | No | |
| Continuous Sunlight | Limited | Limited | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable | |