- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 0.4
- 拉伸強度 [MPa]: 43.4
- 斷裂伸長率 [%]: 9.65
- 彎曲強度 [MPa]: 65.0
- 彎曲模量 [MPa]: 0.945
- 硬度: 100.0
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 1.14 g/cc | 0.0397 - 0.0412 lb/in3 | Average value: 1.13 g/cc Grade Count:28 |
| Water Absorption | 1.50 - 8.00 % | 1.50 - 8.00 % | Average value: 2.35 % Grade Count:23 |
| Linear Mold Shrinkage | 0.00130 - 0.0190 cm/cm | 0.00130 - 0.0190 in/in | Average value: 0.0116 cm/cm Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 - 120 | 100 - 120 | Average value: 115 Grade Count:13 |
| Tensile Strength, Ultimate | 65.0 - 89.6 MPa | 9430 - 13000 psi | Average value: 81.5 MPa Grade Count:8 |
| Tensile Strength, Yield | 43.4 - 90.3 MPa | 6300 - 13100 psi | Average value: 76.2 MPa Grade Count:22 |
| Elongation at Break | 15.0 - 240 % | 15.0 - 240 % | Average value: 73.0 % Grade Count:26 |
| Elongation at Yield | 2.50 - 5.00 % | 2.50 - 5.00 % | Average value: 4.13 % Grade Count:4 |
| Modulus of Elasticity | 1.30 - 3.50 GPa | 189 - 508 ksi | Average value: 2.72 GPa Grade Count:4 |
| Flexural Yield Strength | 9.65 - 124 MPa | 1400 - 18000 psi | Average value: 96.2 MPa Grade Count:23 |
| 30.0 - 30.0 MPa @Temperature 90.0 - 90.0 °C | 4350 - 4350 psi @Temperature 194 - 194 °F | Average value: 30.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.945 - 3.10 GPa | 137 - 450 ksi | Average value: 2.58 GPa Grade Count:25 |
| 0.600 - 0.600 GPa @Temperature 90.0 - 90.0 °C | 87.0 - 87.0 ksi @Temperature 194 - 194 °F | Average value: 0.600 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.400 - 6.41 J/cm | 0.749 - 12.0 ft-lb/in | Average value: 1.12 J/cm Grade Count:23 |
| 3.2034 - 4.53815 J/cm @Temperature -40.0 - -20.0 °C | 6.0013 - 8.50182 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 3.87 J/cm Grade Count:2 | |
| 3.2034 - 4.53815 J/cm @Thickness 3.17 - 3.17 mm | 6.0013 - 8.50182 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 3.87 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 3.00 - 100000 kJ/m2 | 1.43 - 47600 ft-lb/in2 | Average value: 4.00 kJ/m2 Grade Count:4 |
| 3.50 - 3.50 kJ/m2 @Temperature -30.0 - -30.0 °C | 1.67 - 1.67 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 3.50 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 1000 J/cm2 - NB | 4760 ft-lb/in2 - NB | Grade Count:3 |
| >= 25.0 J/cm2 @Temperature -30.0 - -30.0 °C | >= 119 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 25.0 J/cm2 Grade Count:1 | |
| Charpy Impact, Notched | 0.500 J/cm2 - NB | 2.38 ft-lb/in2 - NB | Average value: 0.800 J/cm2 Grade Count:4 |
| 0.300 - 0.300 J/cm2 @Temperature -30.0 - -30.0 °C | 1.43 - 1.43 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.300 J/cm2 Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+15 ohm-cm | 1.00e+13 - 1.00e+15 ohm-cm | Average value: 3.91e+14 ohm-cm Grade Count:12 |
| Dielectric Strength | 14.2 - 30.0 kV/mm | 360 - 762 kV/in | Average value: 18.7 kV/mm Grade Count:13 |
| Comparative Tracking Index | 550 - 600 V | 550 - 600 V | Average value: 590 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 61.2 - 108 μm/m-°C | 34.0 - 60.0 μin/in-°F | Average value: 85.0 μm/m-°C Grade Count:12 |
| Melting Point | 215 - 221 °C | 419 - 430 °F | Average value: 218 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 - 191 °C | 320 - 375 °F | Average value: 178 °C Grade Count:16 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 93.3 °C | 122 - 200 °F | Average value: 69.0 °C Grade Count:24 |
| Vicat Softening Point | 196 - 215 °C | 385 - 419 °F | Average value: 202 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:17 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 295 °C | 446 - 563 °F | Average value: 265 °C Grade Count:4 |
| Nozzle Temperature | 227 - 293 °C | 440 - 560 °F | Average value: 254 °C Grade Count:5 |
| Melt Temperature | 138 - 293 °C | 280 - 560 °F | Average value: 244 °C Grade Count:9 |
| Mold Temperature | 21.1 - 120 °C | 70.0 - 248 °F | Average value: 75.6 °C Grade Count:8 |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | Average value: 78.5 °C Grade Count:9 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.43 hour Grade Count:7 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.171 % Grade Count:3 |
| Injection Pressure | 34.5 - 172 MPa | 5000 - 25000 psi | Average value: 99.6 MPa Grade Count:3 |
| Back Pressure | 0.000 - 0.414 MPa | 0.000 - 60.0 psi | Average value: 0.267 MPa Grade Count:4 |
| Screw Speed | 30.0 - 120 rpm | 30.0 - 120 rpm | Average value: 73.8 rpm Grade Count:4 |