- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 1.0
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 131.0
- 斷裂伸長率 [%]: 82.7
- 彎曲強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 2.41
- 硬度: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 4.00 g/cc | 0.0434 - 0.145 lb/in3 | Average value: 1.75 g/cc Grade Count:7 |
| Filler Content | 7.00 - 15.0 % | 7.00 - 15.0 % | Average value: 10.7 % Grade Count:3 |
| Water Absorption | 1.00 - 1.40 % | 1.00 - 1.40 % | Average value: 1.16 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00200 - 0.0150 cm/cm | 0.00200 - 0.0150 in/in | Average value: 0.00693 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | Average value: 117 Grade Count:3 |
| Tensile Strength, Ultimate | 25.0 - 82.7 MPa | 3630 - 12000 psi | Average value: 60.5 MPa Grade Count:4 |
| Tensile Strength, Yield | 131 - 138 MPa | 19000 - 20000 psi | Average value: 136 MPa Grade Count:3 |
| Elongation at Break | 0.500 - 10.0 % | 0.500 - 10.0 % | Average value: 5.86 % Grade Count:7 |
| Modulus of Elasticity | 2.76 - 7.50 GPa | 400 - 1090 ksi | Average value: 4.12 GPa Grade Count:4 |
| Flexural Yield Strength | 82.7 - 193 MPa | 12000 - 28000 psi | Average value: 151 MPa Grade Count:6 |
| Flexural Modulus | 2.41 - 7.58 GPa | 350 - 1100 ksi | Average value: 5.37 GPa Grade Count:7 |
| Izod Impact, Notched | 0.534 - 2670 J/cm | 1.00 - 5000 ft-lb/in | Average value: 382 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 8.01 - 9.61 J/cm | 15.0 - 18.0 ft-lb/in | Average value: 8.54 J/cm Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 100 ohm-cm | 1.00 - 100 ohm-cm | Average value: 21.3 ohm-cm Grade Count:6 |
| Surface Resistance | 10.0 - 1.00e+6 ohm | 10.0 - 1.00e+6 ohm | Average value: 335000 ohm Grade Count:6 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:6 |
| Shielding Effectiveness | 50.0 dB | 50.0 dB | Average value: 50.0 dB Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 μm/m-°C | 30.0 μin/in-°F | Average value: 54.0 μm/m-°C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 - 210 °C | 180 - 410 °F | Average value: 159 °C Grade Count:5 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 271 °C | 430 - 520 °F | Average value: 246 °C Grade Count:3 |
| Mold Temperature | 54.4 - 93.3 °C | 130 - 200 °F | Average value: 73.5 °C Grade Count:4 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:3 |