- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.3
- 拉伸強度 [MPa]: 29.0
- 斷裂伸長率 [%]: 9.65
- 彎曲強度 [MPa]: 37.9
- 彎曲模量 [MPa]: 0.469
- 硬度: 70.0
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.70 g/cc | 0.0376 - 0.0614 lb/in3 | Average value: 1.27 g/cc Grade Count:234 |
| Filler Content | 13.0 - 40.0 % | 13.0 - 40.0 % | Average value: 32.2 % Grade Count:10 |
| Water Absorption | 0.200 - 10.0 % | 0.200 - 10.0 % | Average value: 1.36 % Grade Count:157 |
| Moisture Absorption at Equilibrium | 0.250 - 2.80 % | 0.250 - 2.80 % | Average value: 2.12 % Grade Count:28 |
| Water Absorption at Saturation | 6.00 - 9.80 % | 6.00 - 9.80 % | Average value: 7.71 % Grade Count:16 |
| Viscosity Measurement | 0.300 - 200 | 0.300 - 200 | Average value: 33.8 Grade Count:15 |
| Linear Mold Shrinkage | 0.00130 - 0.0350 cm/cm | 0.00130 - 0.0350 in/in | Average value: 0.00779 cm/cm Grade Count:198 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0183 cm/cm | 0.00500 - 0.0183 in/in | Average value: 0.0115 cm/cm Grade Count:38 |
| Melt Flow | 1.00 - 100 g/10 min | 1.00 - 100 g/10 min | Average value: 12.3 g/10 min Grade Count:16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70.0 - 212 | 70.0 - 212 | Average value: 115 Grade Count:122 |
| Ball Indentation Hardness | 75.0 - 175 MPa | 10900 - 25400 psi | Average value: 138 MPa Grade Count:12 |
| Tensile Strength, Ultimate | 37.9 - 200 MPa | 5500 - 29000 psi | Average value: 98.3 MPa Grade Count:56 |
| 21.0 - 60.0 MPa @Temperature 60.0 - 120 °C | 3050 - 8700 psi @Temperature 140 - 248 °F | Average value: 40.2 MPa Grade Count:2 | |
| Tensile Strength, Yield | 29.0 - 234 MPa | 4200 - 34000 psi | Average value: 105 MPa Grade Count:184 |
| Elongation at Break | 1.50 - 350 % | 1.50 - 350 % | Average value: 40.2 % Grade Count:203 |
| Elongation at Yield | 2.00 - 200 % | 2.00 - 200 % | Average value: 12.6 % Grade Count:23 |
| Creep Strength | 4.00 - 20.0 MPa | 580 - 2900 psi | Average value: 11.9 MPa Grade Count:10 |
| Modulus of Elasticity | 0.470 - 15.0 GPa | 68.2 - 2180 ksi | Average value: 5.16 GPa Grade Count:54 |
| Flexural Yield Strength | 9.65 - 352 MPa | 1400 - 51000 psi | Average value: 147 MPa Grade Count:211 |
| Flexural Modulus | 0.469 - 20.0 GPa | 68.0 - 2900 ksi | Average value: 4.84 GPa Grade Count:216 |
| 0.450 - 3.70 GPa @Temperature 60.0 - 120 °C | 65.3 - 537 ksi @Temperature 140 - 248 °F | Average value: 1.54 GPa Grade Count:2 | |
| Compressive Yield Strength | 29.0 - 147 MPa | 4210 - 21300 psi | Average value: 66.6 MPa Grade Count:12 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:4 |
| Izod Impact, Notched | 0.300 - 5340 J/cm | 0.562 - 10000 ft-lb/in | Average value: 1.48 J/cm Grade Count:176 |
| 0.250 - 0.300 J/cm @Temperature -40.0 - -20.0 °C | 0.468 - 0.562 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.44 J/cm Grade Count:2 | |
| 0.186865 - 5338.47 J/cm @Temperature -40.0 - -20.0 °C | 0.350075 - 10001.1 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.44 J/cm Grade Count:19 | |
| 0.186865 - 5338.47 J/cm @Thickness 1.57 - 3.17 mm | 0.350075 - 10001.1 ft-lb/in @Thickness 0.0618 - 0.125 in | Average value: 1.44 J/cm Grade Count:19 | |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 6.00 - 10000 ft-lb/in | Average value: 9.90 J/cm Grade Count:46 |
| Izod Impact, Notched (ISO) | 2.50 - 100000 kJ/m2 | 1.19 - 47600 ft-lb/in2 | Average value: 15.3 kJ/m2 Grade Count:28 |
| 5.00 - 20.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 2.38 - 9.52 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 10.9 kJ/m2 Grade Count:14 | |
| Izod Impact, Unnotched (ISO) | 30.0 - 110 kJ/m2 | 14.3 - 52.3 ft-lb/in2 | Average value: 66.5 kJ/m2 Grade Count:10 |
| 30.0 - 100 kJ/m2 @Temperature -30.0 - -30.0 °C | 14.3 - 47.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 55.8 kJ/m2 Grade Count:10 | |
| Charpy Impact Unnotched | 2.00 J/cm2 - NB | 9.52 ft-lb/in2 - NB | Average value: 6.58 J/cm2 Grade Count:29 |
| 1.50 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 7.14 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 4.89 J/cm2 Grade Count:24 | |
| Charpy Impact, Notched | 0.150 - 13.0 J/cm2 | 0.714 - 61.9 ft-lb/in2 | Average value: 1.65 J/cm2 Grade Count:28 |
| 0.150 - 2.00 J/cm2 @Temperature -30.0 - -20.0 °C | 0.714 - 9.52 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.804 J/cm2 Grade Count:24 | |
| Puncture Energy | 64.0 - 64.0 J @Temperature -30.0 - -30.0 °C | 47.2 - 47.2 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 64.0 J Grade Count:1 |
| Coefficient of Friction | 0.0400 - 0.390 | 0.0400 - 0.390 | Average value: 0.204 Grade Count:14 |
| Tear Strength Test | 0.150 - 0.250 | 0.150 - 0.250 | Average value: 0.190 Grade Count:10 |
| K Factor (Wear Factor) | 9.00e-11 - 0.440 | 9.00e-11 - 0.440 | Average value: 0.0400 Grade Count:11 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 5.00e+15 ohm-cm | 1.00 - 5.00e+15 ohm-cm | Average value: 5.85e+14 ohm-cm Grade Count:143 |
| Surface Resistance | 1.00 - 1.00e+15 ohm | 1.00 - 1.00e+15 ohm | Average value: 1.01e+14 ohm Grade Count:48 |
| Dielectric Constant | 3.00 - 4.00 | 3.00 - 4.00 | Average value: 3.63 Grade Count:15 |
| Dielectric Strength | 15.4 - 80.0 kV/mm | 390 - 2030 kV/in | Average value: 20.3 kV/mm Grade Count:132 |
| Dielectric Loss Index | 0.0300 | 0.0300 | Average value: 0.0300 Grade Count:10 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Average value: 566 V Grade Count:23 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.20 - 150 μm/m-°C | 4.00 - 83.3 μin/in-°F | Average value: 49.9 μm/m-°C Grade Count:139 |
| CTE, linear, Transverse to Flow | 90.0 - 150 μm/m-°C | 50.0 - 83.3 μin/in-°F | Average value: 108 μm/m-°C Grade Count:5 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Average value: 1.67 J/g-°C Grade Count:10 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | Average value: 0.250 W/m-K Grade Count:10 |
| Melting Point | 215 - 260 °C | 419 - 500 °F | Average value: 221 °C Grade Count:79 |
| Maximum Service Temperature, Air | 115 - 190 °C | 239 - 374 °F | Average value: 149 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 - 221 °C | 203 - 430 °F | Average value: 199 °C Grade Count:150 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 - 250 °C | 120 - 482 °F | Average value: 142 °C Grade Count:209 |
| Vicat Softening Point | 190 - 255 °C | 374 - 491 °F | Average value: 206 °C Grade Count:29 |
| Minimum Service Temperature, Air | -100 - -40.0 °C | -148 - -40.0 °F | Average value: -45.0 °C Grade Count:11 |
| UL RTI, Electrical | 120 °C | 248 °F | Average value: 120 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | Average value: 120 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | Average value: 115 °C Grade Count:3 |
| Flammability, UL94 | HB - 5VB | HB - 5VB | Grade Count:108 |
| Oxygen Index | 26.0 - 30.0 % | 26.0 - 30.0 % | Average value: 28.3 % Grade Count:3 |
| Glow Wire Test | 192 - 960 °C | 378 - 1760 °F | Average value: 788 °C Grade Count:21 |
| Shrinkage | 0.0700 - 0.200 % | 0.0700 - 0.200 % | Average value: 0.143 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 275 °C | 446 - 527 °F | Average value: 249 °C Grade Count:26 |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Average value: 70.0 °C Grade Count:10 |
| Nozzle Temperature | 227 - 293 °C | 440 - 560 °F | Average value: 251 °C Grade Count:13 |
| Melt Temperature | 138 - 293 °C | 280 - 560 °F | Average value: 254 °C Grade Count:73 |
| Mold Temperature | 21.1 - 121 °C | 70.0 - 250 °F | Average value: 78.7 °C Grade Count:84 |
| Drying Temperature | 73.9 - 100 °C | 165 - 212 °F | Average value: 78.6 °C Grade Count:67 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.29 hour Grade Count:52 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.42 hour Grade Count:19 | |
| Moisture Content | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.157 % Grade Count:59 |
| Injection Pressure | 3.45 - 172 MPa | 500 - 25000 psi | Average value: 43.8 MPa Grade Count:34 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:10 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.450 MPa Grade Count:37 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:13 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 73.9 rpm Grade Count:37 |