- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.13
- 缺口沖擊強度: 0.4
- 拉伸強度 [MPa]: 50.0
- 斷裂伸長率 [%]: 65.0
- 彎曲強度 [MPa]: 31.8
- 彎曲模量 [MPa]: 0.0216
- 硬度: 90.0
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.67 g/cc | 0.0410 - 0.0603 lb/in3 | Average value: 1.37 g/cc Grade Count:577 |
| Filler Content | 13.0 - 35.0 % | 13.0 - 35.0 % | Average value: 30.1 % Grade Count:92 |
| Water Absorption | 0.130 - 9.00 % | 0.130 - 9.00 % | Average value: 3.08 % Grade Count:325 |
| Moisture Absorption at Equilibrium | 0.170 - 7.10 % | 0.170 - 7.10 % | Average value: 1.84 % Grade Count:219 |
| Water Absorption at Saturation | 5.00 - 8.20 % | 5.00 - 8.20 % | Average value: 6.65 % Grade Count:41 |
| 0.500 - 2.15 % @Temperature 30.0 - 405 °C | 0.500 - 2.15 % @Temperature 86.0 - 761 °F | Average value: 1.70 % Grade Count:1 | |
| Viscosity | 2.60 - 50.0 cP | 2.60 - 50.0 cP | Average value: 9.37 cP Grade Count:7 |
| 30.0 - 500 cP @Temperature 230 - 270 °C | 30.0 - 500 cP @Temperature 446 - 518 °F | Average value: 188 cP Grade Count:2 | |
| 30.0 - 500 cP @Shear Rate 100 - 10000 1/s | 30.0 - 500 cP @Shear Rate 100 - 10000 1/s | Average value: 188 cP Grade Count:2 | |
| Viscosity Measurement | 0.400 - 160 | 0.400 - 160 | Average value: 92.7 Grade Count:57 |
| Viscosity Test | 104 - 195 cm3/g | 104 - 195 cm3/g | Average value: 143 cm3/g Grade Count:30 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:42 |
| Linear Mold Shrinkage | 0.000300 - 0.0350 cm/cm | 0.000300 - 0.0350 in/in | Average value: 0.00430 cm/cm Grade Count:421 |
| 0.00280 - 0.00400 cm/cm @Temperature 80.0 - 80.0 °C | 0.00280 - 0.00400 in/in @Temperature 176 - 176 °F | Average value: 0.00304 cm/cm Grade Count:20 | |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | Average value: 0.00489 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.000900 - 0.0170 cm/cm | 0.000900 - 0.0170 in/in | Average value: 0.00831 cm/cm Grade Count:141 |
| 0.00600 - 0.00800 cm/cm @Temperature 80.0 - 80.0 °C | 0.00600 - 0.00800 in/in @Temperature 176 - 176 °F | Average value: 0.00695 cm/cm Grade Count:20 | |
| Melt Flow | 1.00 - 101 g/10 min | 1.00 - 101 g/10 min | Average value: 31.5 g/10 min Grade Count:83 |
| Spiral Flow | 655 - 715 cm | 258 - 281 in | Average value: 693 cm Grade Count:4 |
| Ash | 30.0 - 33.1 % | 30.0 - 33.1 % | Average value: 31.2 % Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 111 - 115 | 111 - 115 | Average value: 114 Grade Count:5 |
| Hardness, Rockwell M | 94.0 - 100 | 94.0 - 100 | Average value: 97.3 Grade Count:8 |
| Hardness, Rockwell R | 90.0 - 122 | 90.0 - 122 | Average value: 119 Grade Count:123 |
| Hardness, Shore D | 67.0 - 94.0 | 67.0 - 94.0 | Average value: 85.1 Grade Count:30 |
| Ball Indentation Hardness | 70.0 - 230 MPa | 10200 - 33400 psi | Average value: 153 MPa Grade Count:34 |
| Tensile Strength, Ultimate | 31.8 - 203 MPa | 4610 - 29500 psi | Average value: 140 MPa Grade Count:394 |
| 43.0 - 283 MPa @Temperature -40.0 - 121 °C | 6240 - 41000 psi @Temperature -40.0 - 250 °F | Average value: 102 MPa Grade Count:15 | |
| 50.0 - 92.5 MPa @Temperature 130 - 175 °C | 7250 - 13400 psi @Temperature 266 - 347 °F | Average value: 102 MPa Grade Count:4 | |
| 50.0 - 92.5 MPa @Time 1.80e+7 - 7.20e+7 sec | 7250 - 13400 psi @Time 5000 - 20000 hour | Average value: 102 MPa Grade Count:4 | |
| 21.8 - 207 MPa @Strain 0.210 - 3.50 % | 3160 - 30000 psi @Strain 0.210 - 3.50 % | Average value: 102 MPa Grade Count:2 | |
| 21.8 - 207 MPa @Temperature -20.0 - 150 °C | 3160 - 30000 psi @Temperature -4.00 - 302 °F | Average value: 102 MPa Grade Count:2 | |
| Tensile Strength, Yield | 50.0 - 193 MPa | 7250 - 28000 psi | Average value: 149 MPa Grade Count:185 |
| 111 - 214 MPa @Temperature -40.0 - 80.0 °C | 16100 - 31000 psi @Temperature -40.0 - 176 °F | Average value: 176 MPa Grade Count:2 | |
| Elongation at Break | 1.00 - 142 % | 1.00 - 142 % | Average value: 4.40 % Grade Count:479 |
| 2.50 - 7.00 % @Temperature -40.0 - 121 °C | 2.50 - 7.00 % @Temperature -40.0 - 250 °F | Average value: 5.28 % Grade Count:5 | |
| Elongation at Yield | 2.00 - 10.0 % | 2.00 - 10.0 % | Average value: 4.02 % Grade Count:89 |
| Modulus of Elasticity | 0.700 - 15.0 GPa | 102 - 2180 ksi | Average value: 7.93 GPa Grade Count:330 |
| 2.66 - 11.6 GPa @Temperature -40.0 - 121 °C | 386 - 1680 ksi @Temperature -40.0 - 250 °F | Average value: 6.31 GPa Grade Count:8 | |
| Flexural Yield Strength | 65.0 - 301 MPa | 9430 - 43600 psi | Average value: 216 MPa Grade Count:407 |
| 89.0 - 380 MPa @Temperature -40.0 - 121 °C | 12900 - 55100 psi @Temperature -40.0 - 250 °F | Average value: 186 MPa Grade Count:9 | |
| Flexural Modulus | 0.0216 - 14.3 GPa | 3.13 - 2070 ksi | Average value: 7.17 GPa Grade Count:443 |
| 2.80 - 12.5 GPa @Temperature -40.0 - 121 °C | 406 - 1810 ksi @Temperature -40.0 - 250 °F | Average value: 4.92 GPa Grade Count:13 | |
| Compressive Yield Strength | 140 - 222 MPa | 20300 - 32200 psi | Average value: 166 MPa Grade Count:10 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:8 |
| Shear Modulus | 1.66 - 4.10 GPa | 240 - 595 ksi | Average value: 3.10 GPa Grade Count:6 |
| 0.000 - 2.081 GPa @Temperature -50.0 - 228 °C | 0.000 - 301.8 ksi @Temperature -58.0 - 442 °F | Average value: 0.874 GPa Grade Count:2 | |
| Izod Impact, Notched | 0.400 - 3.36 J/cm | 0.749 - 6.30 ft-lb/in | Average value: 1.27 J/cm Grade Count:255 |
| 0.400 - 3.84408 J/cm @Temperature -40.0 - 121 °C | 0.749 - 7.20154 ft-lb/in @Temperature -40.0 - 250 °F | Average value: 1.10 J/cm Grade Count:11 | |
| 1.01441 - 1.33475 J/cm @Temperature -40.0 - -40.0 °C | 1.90041 - 2.50053 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.10 J/cm Grade Count:7 | |
| 1.01441 - 1.33475 J/cm @Thickness 3.17 - 3.17 mm | 1.90041 - 2.50053 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.10 J/cm Grade Count:7 | |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 6.00 - 10000 ft-lb/in | Average value: 10.4 J/cm Grade Count:51 |
| Izod Impact, Notched (ISO) | 1.50 - 182 kJ/m2 | 0.714 - 86.6 ft-lb/in2 | Average value: 18.9 kJ/m2 Grade Count:141 |
| 3.00 - 18.0 kJ/m2 @Temperature -40.0 - -20.0 °C | 1.43 - 8.57 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 11.0 kJ/m2 Grade Count:41 | |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m2 - NB | 5.71 ft-lb/in2 - NB | Average value: 68.1 kJ/m2 Grade Count:36 |
| 40.0 kJ/m2 - NB @Temperature -30.0 - -30.0 °C | 19.0 ft-lb/in2 - NB @Temperature -22.0 - -22.0 °F | Average value: 69.1 kJ/m2 Grade Count:23 | |
| Charpy Impact Unnotched | 2.30 J/cm2 - NB | 10.9 ft-lb/in2 - NB | Average value: 7.76 J/cm2 Grade Count:255 |
| 2.00 J/cm2 - NB @Temperature -40.0 - 30.0 °C | 9.52 ft-lb/in2 - NB @Temperature -40.0 - 86.0 °F | Average value: 6.10 J/cm2 Grade Count:150 | |
| Charpy Impact, Notched | 0.200 - 1000 J/cm2 | 0.952 - 4760 ft-lb/in2 | Average value: 1.55 J/cm2 Grade Count:264 |
| 0.150 - 19.0 J/cm2 @Temperature -40.0 - 30.0 °C | 0.714 - 90.4 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 1.20 J/cm2 Grade Count:156 | |
| Puncture Energy | 2.00 - 14.0 J | 1.48 - 10.3 ft-lb | Average value: 5.86 J Grade Count:19 |
| 1.70 - 6.00 J @Temperature -30.0 - -30.0 °C | 1.25 - 4.43 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 3.13 J Grade Count:17 | |
| 2.00 - 2.00 J @Temperature -30.0 - -30.0 °C | 1.48 - 1.48 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 3.13 J Grade Count:1 | |
| 2.00 - 2.00 J @Load <=75.5 kg | 1.48 - 1.48 ft-lb @Load <=166 lb | Average value: 3.13 J Grade Count:1 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 92000 MPa | 0.000 - 1.33e+7 psi | Average value: 4840 MPa Grade Count:19 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 90.0 °C | 0.000 - 8700 psi @Temperature 140 - 194 °F | Average value: 24.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 1.88 % | 0.000 - 8700 psi @Strain 0.000 - 1.88 % | Average value: 24.0 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 6500 MPa | 0.000 - 943000 psi | Average value: 1560 MPa Grade Count:21 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 90.0 °C | 0.000 - 8700 psi @Temperature 140 - 194 °F | Average value: 24.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 2.55 % | 0.000 - 8700 psi @Strain 0.000 - 2.55 % | Average value: 24.0 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2500 - 1.00e+17 ohm-cm | 2500 - 1.00e+17 ohm-cm | Average value: 9.17e+14 ohm-cm Grade Count:264 |
| Surface Resistance | 10000 - 1.00e+16 ohm | 10000 - 1.00e+16 ohm | Average value: 3.62e+14 ohm Grade Count:139 |
| Dielectric Constant | 2.60 - 38.0 | 2.60 - 38.0 | Average value: 5.60 Grade Count:132 |
| Dielectric Strength | 11.0 - 80.0 kV/mm | 280 - 2030 kV/in | Average value: 29.8 kV/mm Grade Count:196 |
| Dissipation Factor | 0.00500 - 0.850 | 0.00500 - 0.850 | Average value: 0.0798 Grade Count:114 |
| Dielectric Loss Index | 0.0220 - 0.240 | 0.0220 - 0.240 | Average value: 0.125 Grade Count:10 |
| Arc Resistance | 15.0 - 180 sec | 15.0 - 180 sec | Average value: 112 sec Grade Count:19 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 513 V Grade Count:182 |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 150 mm/min | 1.00 - 5.91 in/min | Average value: 63.5 mm/min Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.150 - 500 μm/m-°C | 0.0833 - 278 μin/in-°F | Average value: 53.6 μm/m-°C Grade Count:190 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:3 | |
| CTE, linear, Transverse to Flow | 0.250 - 150 μm/m-°C | 0.139 - 83.3 μin/in-°F | Average value: 75.1 μm/m-°C Grade Count:88 |
| 110 - 125 μm/m-°C @Temperature 55.0 - 160 °C | 61.1 - 69.4 μin/in-°F @Temperature 131 - 320 °F | Average value: 118 μm/m-°C Grade Count:3 | |
| Specific Heat Capacity | 0.350 - 2.43 J/g-°C | 0.0837 - 0.582 BTU/lb-°F | Average value: 1.57 J/g-°C Grade Count:22 |
| Thermal Conductivity | 0.200 - 1.64 W/m-K | 1.39 - 11.4 BTU-in/hr-ft2-°F | Average value: 0.361 W/m-K Grade Count:38 |
| Melting Point | 208 - 295 °C | 406 - 563 °F | Average value: 221 °C Grade Count:351 |
| Maximum Service Temperature, Air | 65.0 - 270 °C | 149 - 518 °F | Average value: 154 °C Grade Count:76 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 240 °C | 257 - 464 °F | Average value: 215 °C Grade Count:296 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 - 270 °C | 129 - 518 °F | Average value: 204 °C Grade Count:488 |
| Deflection Temperature at 8.0 MPa | 60.0 - 187 °C | 140 - 369 °F | Average value: 111 °C Grade Count:31 |
| Vicat Softening Point | 183 - 250 °C | 361 - 482 °F | Average value: 206 °C Grade Count:110 |
| Decomposition Temperature | 300 - 350 °C | 572 - 662 °F | Average value: 321 °C Grade Count:20 |
| UL RTI, Electrical | 65.0 - 140 °C | 149 - 284 °F | Average value: 104 °C Grade Count:32 |
| UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 95.7 °C Grade Count:32 |
| UL RTI, Mechanical without Impact | 65.0 - 150 °C | 149 - 302 °F | Average value: 104 °C Grade Count:31 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:343 |
| Flammability Test | 1.00 - 165 | 1.00 - 165 | Average value: 46.8 Grade Count:4 |
| Oxygen Index | 3.20 - 35.0 % | 3.20 - 35.0 % | Average value: 24.2 % Grade Count:35 |
| Glow Wire Test | 550 - 960 °C | 1020 - 1760 °F | Average value: 782 °C Grade Count:76 |
| Shrinkage | 0.0400 - 0.160 % | 0.0400 - 0.160 % | Average value: 0.0887 % Grade Count:4 |
| 0.0700 - 0.150 % @Temperature 120 - 120 °C | 0.0700 - 0.150 % @Temperature 248 - 248 °F | Average value: 0.105 % Grade Count:2 | |
| 0.0700 - 0.150 % @Time 14400 - 14400 sec | 0.0700 - 0.150 % @Time 4.00 - 4.00 hour | Average value: 0.105 % Grade Count:2 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 300 °C | 158 - 572 °F | Average value: 206 °C Grade Count:52 |
| Feed Temperature | 20.0 - 260 °C | 68.0 - 500 °F | Average value: 160 °C Grade Count:30 |
| Nozzle Temperature | 210 - 293 °C | 410 - 560 °F | Average value: 259 °C Grade Count:29 |
| Melt Temperature | 80.0 - 330 °C | 176 - 626 °F | Average value: 255 °C Grade Count:256 |
| Mold Temperature | 21.1 - 121 °C | 70.0 - 250 °F | Average value: 84.1 °C Grade Count:235 |
| Drying Temperature | 70.0 - 130 °C | 158 - 266 °F | Average value: 82.6 °C Grade Count:204 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.89 hour Grade Count:157 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.50 hour Grade Count:10 | |
| Moisture Content | 0.00300 - 1.90 % | 0.00300 - 1.90 % | Average value: 0.177 % Grade Count:127 |
| Dew Point | -30.0 - -17.8 °C | -22.0 - 0.000 °F | Average value: -19.1 °C Grade Count:9 |
| Injection Pressure | 4.96 - 172 MPa | 720 - 25000 psi | Average value: 77.7 MPa Grade Count:68 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:10 |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | Average value: 0.564 MPa Grade Count:19 |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Average value: 400 mm/sec Grade Count:3 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 53.6 % Grade Count:7 |
| Screw Speed | 20.0 - 200 rpm | 20.0 - 200 rpm | Average value: 69.2 rpm Grade Count:16 |