- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 0.7
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 45.0
- 斷裂伸長率 [%]: 50.0
- 彎曲強度 [MPa]: 17.2
- 彎曲模量 [MPa]: 0.0755
- 硬度: 116.0
- 熱變形溫度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 - 1.61 g/cc | 0.0466 - 0.0582 lb/in3 | Average value: 1.47 g/cc Grade Count:57 |
| Filler Content | 35.0 - 40.0 % | 35.0 - 40.0 % | Average value: 39.6 % Grade Count:18 |
| Water Absorption | 0.700 - 6.00 % | 0.700 - 6.00 % | Average value: 2.42 % Grade Count:38 |
| Moisture Absorption at Equilibrium | 0.250 - 2.30 % | 0.250 - 2.30 % | Average value: 1.57 % Grade Count:22 |
| Water Absorption at Saturation | 5.70 - 7.00 % | 5.70 - 7.00 % | Average value: 6.07 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00100 - 0.0180 cm/cm | 0.00100 - 0.0180 in/in | Average value: 0.00751 cm/cm Grade Count:48 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0122 cm/cm | 0.00200 - 0.0122 in/in | Average value: 0.00856 cm/cm Grade Count:10 |
| Melt Flow | 3.00 - 33.0 g/10 min | 3.00 - 33.0 g/10 min | Average value: 19.0 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 95.0 | 90.0 - 95.0 | Average value: 93.3 Grade Count:3 |
| Hardness, Rockwell R | 116 - 122 | 116 - 122 | Average value: 120 Grade Count:16 |
| Ball Indentation Hardness | 85.0 - 205 MPa | 12300 - 29700 psi | Average value: 140 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 17.2 - 98.1 MPa | 2500 - 14200 psi | Average value: 65.7 MPa Grade Count:36 |
| 20.0 - 135 MPa @Temperature -40.0 - 120 °C | 2900 - 19600 psi @Temperature -40.0 - 248 °F | Average value: 51.3 MPa Grade Count:7 | |
| 4.89 - 138.48 MPa @Temperature -40.0 - 150 °C | 709 - 20085 psi @Temperature -40.0 - 302 °F | Average value: 51.3 MPa Grade Count:1 | |
| 4.89 - 138.48 MPa @Strain 0.200 - 29.2 % | 709 - 20085 psi @Strain 0.200 - 29.2 % | Average value: 51.3 MPa Grade Count:1 | |
| Tensile Strength, Yield | 45.0 - 120 MPa | 6530 - 17400 psi | Average value: 82.0 MPa Grade Count:24 |
| 20.0 - 90.0 MPa @Temperature -40.0 - 120 °C | 2900 - 13100 psi @Temperature -40.0 - 248 °F | Average value: 45.0 MPa Grade Count:1 | |
| Elongation at Break | 1.50 - 40.0 % | 1.50 - 40.0 % | Average value: 15.3 % Grade Count:43 |
| 5.00 - 40.0 % @Temperature -40.0 - 120 °C | 5.00 - 40.0 % @Temperature -40.0 - 248 °F | Average value: 25.6 % Grade Count:3 | |
| Elongation at Yield | 2.50 - 27.0 % | 2.50 - 27.0 % | Average value: 7.84 % Grade Count:16 |
| 5.10 - 30.0 % @Temperature -40.0 - 120 °C | 5.10 - 30.0 % @Temperature -40.0 - 248 °F | Average value: 20.0 % Grade Count:1 | |
| Modulus of Elasticity | 2.20 - 7.58 GPa | 319 - 1100 ksi | Average value: 4.74 GPa Grade Count:26 |
| 0.600 - 8.31 GPa @Temperature -40.0 - 120 °C | 87.0 - 1210 ksi @Temperature -40.0 - 248 °F | Average value: 3.30 GPa Grade Count:4 | |
| Flexural Yield Strength | 50.0 - 250 MPa | 7250 - 36300 psi | Average value: 118 MPa Grade Count:42 |
| 25.0 - 207 MPa @Temperature -40.0 - 120 °C | 3630 - 30000 psi @Temperature -40.0 - 248 °F | Average value: 84.2 MPa Grade Count:6 | |
| Flexural Modulus | 0.0755 - 7.88 GPa | 11.0 - 1140 ksi | Average value: 5.06 GPa Grade Count:48 |
| 0.700 - 8.60 GPa @Temperature -40.0 - 120 °C | 102 - 1250 ksi @Temperature -40.0 - 248 °F | Average value: 2.76 GPa Grade Count:7 | |
| Compressive Yield Strength | 69.0 - 186 MPa | 10000 - 27000 psi | Average value: 124 MPa Grade Count:5 |
| Izod Impact, Notched | 0.267 - 100 J/cm | 0.500 - 187 ft-lb/in | Average value: 0.669 J/cm Grade Count:34 |
| 0.320 - 0.820 J/cm @Temperature -40.0 - -40.0 °C | 0.599 - 1.54 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.578 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 2.14 - 16.4 J/cm | 4.00 - 30.7 ft-lb/in | Average value: 6.39 J/cm Grade Count:8 |
| Izod Impact, Notched (ISO) | 3.90 - 10.0 kJ/m2 | 1.86 - 4.76 ft-lb/in2 | Average value: 7.32 kJ/m2 Grade Count:6 |
| 4.00 - 10.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 1.90 - 4.76 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 8.08 kJ/m2 Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 75.0 - 85.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 35.7 - 40.4 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 80.0 kJ/m2 Grade Count:2 |
| Charpy Impact Unnotched | 1.70 J/cm2 - NB | 8.09 ft-lb/in2 - NB | Average value: 10.1 J/cm2 Grade Count:16 |
| 1.80 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 8.57 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 7.38 J/cm2 Grade Count:8 | |
| Charpy Impact, Notched | 0.300 - 1.20 J/cm2 | 1.43 - 5.71 ft-lb/in2 | Average value: 0.775 J/cm2 Grade Count:17 |
| 0.270 - 1.00 J/cm2 @Temperature -40.0 - -20.0 °C | 1.28 - 4.76 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 0.734 J/cm2 Grade Count:10 | |
| Puncture Energy | 9.20 - 65.0 J | 6.79 - 47.9 ft-lb | Average value: 37.7 J Grade Count:4 |
| 1.60 - 3.00 J @Temperature -30.0 - -30.0 °C | 1.18 - 2.21 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.65 J Grade Count:2 | |
| 3.00 - 3.00 J @Temperature -30.0 - -30.0 °C | 2.21 - 2.21 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.65 J Grade Count:2 | |
| 3.00 - 3.00 J @Load <=74.2 kg | 2.21 - 2.21 ft-lb @Load <=164 lb | Average value: 2.65 J Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+16 ohm-cm | 1.00e+9 - 1.00e+16 ohm-cm | Average value: 9.30e+14 ohm-cm Grade Count:22 |
| Surface Resistance | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | Average value: 3.04e+13 ohm Grade Count:7 |
| Dielectric Constant | 3.80 - 15.0 | 3.80 - 15.0 | Average value: 5.76 Grade Count:8 |
| Dielectric Strength | 16.0 - 38.0 kV/mm | 406 - 965 kV/in | Average value: 25.5 kV/mm Grade Count:15 |
| Dissipation Factor | 0.0110 - 0.250 | 0.0110 - 0.250 | Average value: 0.0625 Grade Count:7 |
| Arc Resistance | 115 - 190 sec | 115 - 190 sec | Average value: 138 sec Grade Count:6 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Average value: 525 V Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.20 - 500 μm/m-°C | 4.00 - 278 μin/in-°F | Average value: 83.2 μm/m-°C Grade Count:24 |
| CTE, linear, Transverse to Flow | 58.0 - 75.0 μm/m-°C | 32.2 - 41.7 μin/in-°F | Average value: 67.1 μm/m-°C Grade Count:8 |
| Specific Heat Capacity | 2.00 - 2.00 J/g-°C | 0.478 - 0.478 BTU/lb-°F | Average value: 2.00 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.281 - 1.22 W/m-K | 1.95 - 8.50 BTU-in/hr-ft2-°F | Average value: 0.460 W/m-K Grade Count:7 |
| Melting Point | 215 - 222 °C | 419 - 432 °F | Average value: 219 °C Grade Count:37 |
| Maximum Service Temperature, Air | 65.0 - 120 °C | 149 - 248 °F | Average value: 100 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 - 220 °C | 360 - 428 °F | Average value: 199 °C Grade Count:30 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 204 °C | 176 - 400 °F | Average value: 128 °C Grade Count:48 |
| Vicat Softening Point | 200 - 225 °C | 392 - 437 °F | Average value: 204 °C Grade Count:11 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:29 |
| Oxygen Index | 24.0 - 28.0 % | 24.0 - 28.0 % | Average value: 26.4 % Grade Count:5 |
| Glow Wire Test | 650 °C | 1200 °F | Average value: 650 °C Grade Count:5 |
| Shrinkage | 0.300 - 0.300 % @Temperature 120 - 120 °C | 0.300 - 0.300 % @Temperature 248 - 248 °F | Average value: 0.300 % Grade Count:1 |
| 0.300 - 0.300 % @Time 14400 - 14400 sec | 0.300 - 0.300 % @Time 4.00 - 4.00 hour | Average value: 0.300 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 290 °C | 430 - 554 °F | Average value: 263 °C Grade Count:7 |
| Nozzle Temperature | 254 - 293 °C | 490 - 560 °F | Average value: 268 °C Grade Count:4 |
| Melt Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 263 °C Grade Count:27 |
| Mold Temperature | 54.4 - 121 °C | 130 - 250 °F | Average value: 88.1 °C Grade Count:32 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 83.3 °C Grade Count:11 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.45 hour Grade Count:10 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:2 | |
| Moisture Content | 0.0300 - 1.12 % | 0.0300 - 1.12 % | Average value: 0.229 % Grade Count:5 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 52.2 MPa Grade Count:10 |
| Back Pressure | 0.345 MPa | 50.0 psi | Average value: 0.345 MPa Grade Count:3 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 65.0 rpm Grade Count:3 |