- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.3
- 拉伸強度 [MPa]: 60.0
- 斷裂伸長率 [%]: 55.0
- 彎曲強度 [MPa]: 13.8
- 彎曲模量 [MPa]: 0.0628
- 硬度: 90.0
- 熱變形溫度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.67 g/cc | 0.0412 - 0.0603 lb/in3 | Average value: 1.26 g/cc Grade Count:301 |
| Filler Content | 15.0 - 25.0 % | 15.0 - 25.0 % | Average value: 18.4 % Grade Count:46 |
| Water Absorption | 0.150 - 9.50 % | 0.150 - 9.50 % | Average value: 3.54 % Grade Count:157 |
| Moisture Absorption at Equilibrium | 0.170 - 8.00 % | 0.170 - 8.00 % | Average value: 2.43 % Grade Count:90 |
| Water Absorption at Saturation | 6.00 - 9.00 % | 6.00 - 9.00 % | Average value: 7.64 % Grade Count:22 |
| Viscosity Measurement | 0.300 - 170 | 0.300 - 170 | Average value: 82.9 Grade Count:32 |
| Viscosity Test | 140 - 150 cm3/g | 140 - 150 cm3/g | Average value: 148 cm3/g Grade Count:8 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:6 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00525 cm/cm Grade Count:229 |
| 0.00400 - 0.00700 cm/cm @Temperature 80.0 - 80.0 °C | 0.00400 - 0.00700 in/in @Temperature 176 - 176 °F | Average value: 0.00567 cm/cm Grade Count:3 | |
| Linear Mold Shrinkage, 6.35 mm section | 0.00600 - 0.00800 cm/cm | 0.00600 - 0.00800 in/in | Average value: 0.00700 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00160 - 0.0197 cm/cm | 0.00160 - 0.0197 in/in | Average value: 0.00936 cm/cm Grade Count:83 |
| 0.00800 - 0.0100 cm/cm @Temperature 80.0 - 80.0 °C | 0.00800 - 0.0100 in/in @Temperature 176 - 176 °F | Average value: 0.00867 cm/cm Grade Count:3 | |
| Melt Flow | 1.00 - 92.3 g/10 min | 1.00 - 92.3 g/10 min | Average value: 24.5 g/10 min Grade Count:50 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 100 | 80.0 - 100 | Average value: 91.1 Grade Count:9 |
| Hardness, Rockwell R | 90.0 - 122 | 90.0 - 122 | Average value: 117 Grade Count:59 |
| Hardness, Shore D | 73.0 - 91.0 | 73.0 - 91.0 | Average value: 79.5 Grade Count:11 |
| Ball Indentation Hardness | 70.0 - 185 MPa | 10200 - 26800 psi | Average value: 136 MPa Grade Count:17 |
| Tensile Strength, Ultimate | 13.8 - 180 MPa | 2000 - 26100 psi | Average value: 106 MPa Grade Count:220 |
| 35.0 - 163 MPa @Temperature -40.0 - 120 °C | 5080 - 23600 psi @Temperature -40.0 - 248 °F | Average value: 58.3 MPa Grade Count:6 | |
| 37.5 - 75.0 MPa @Temperature 130 - 175 °C | 5440 - 10900 psi @Temperature 266 - 347 °F | Average value: 58.3 MPa Grade Count:4 | |
| 37.5 - 75.0 MPa @Time 1.80e+7 - 7.20e+7 sec | 5440 - 10900 psi @Time 5000 - 20000 hour | Average value: 58.3 MPa Grade Count:4 | |
| 4.30 - 175 MPa @Strain 0.210 - 6.93 % | 624 - 25400 psi @Strain 0.210 - 6.93 % | Average value: 58.3 MPa Grade Count:1 | |
| 4.30 - 175 MPa @Temperature -40.0 - 150 °C | 624 - 25400 psi @Temperature -40.0 - 302 °F | Average value: 58.3 MPa Grade Count:1 | |
| Tensile Strength, Yield | 60.0 - 195 MPa | 8700 - 28300 psi | Average value: 113 MPa Grade Count:84 |
| 53.0 - 53.0 MPa @Temperature 80.0 - 80.0 °C | 7690 - 7690 psi @Temperature 176 - 176 °F | Average value: 53.0 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 28.0 % | 1.00 - 28.0 % | Average value: 5.13 % Grade Count:256 |
| 4.50 - 5.20 % @Temperature -40.0 - -40.0 °C | 4.50 - 5.20 % @Temperature -40.0 - -40.0 °F | Average value: 4.85 % Grade Count:2 | |
| Elongation at Yield | 2.00 - 18.0 % | 2.00 - 18.0 % | Average value: 6.31 % Grade Count:27 |
| 8.60 - 8.60 % @Temperature 80.0 - 80.0 °C | 8.60 - 8.60 % @Temperature 176 - 176 °F | Average value: 8.60 % Grade Count:1 | |
| Modulus of Elasticity | 1.00 - 14.3 GPa | 145 - 2070 ksi | Average value: 5.39 GPa Grade Count:179 |
| Flexural Yield Strength | 55.0 - 300 MPa | 7980 - 43500 psi | Average value: 165 MPa Grade Count:197 |
| 45.0 - 240 MPa @Temperature -40.0 - 90.0 °C | 6530 - 34800 psi @Temperature -40.0 - 194 °F | Average value: 116 MPa Grade Count:4 | |
| Flexural Modulus | 0.0628 - 10.3 GPa | 9.10 - 1490 ksi | Average value: 4.98 GPa Grade Count:213 |
| 1.70 - 8.00 GPa @Temperature -40.0 - 120 °C | 247 - 1160 ksi @Temperature -40.0 - 248 °F | Average value: 3.83 GPa Grade Count:5 | |
| Compressive Yield Strength | 103 - 145 MPa | 14900 - 21000 psi | Average value: 127 MPa Grade Count:9 |
| Poissons Ratio | 0.350 | 0.350 | Average value: 0.350 Grade Count:4 |
| Shear Modulus | 1.37 - 2.60 GPa | 199 - 377 ksi | Average value: 2.23 GPa Grade Count:5 |
| 0.0170 - 1.557 GPa @Temperature -50.0 - 226 °C | 2.47 - 225.8 ksi @Temperature -58.0 - 439 °F | Average value: 0.709 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.300 - 2.51 J/cm | 0.562 - 4.70 ft-lb/in | Average value: 0.870 J/cm Grade Count:121 |
| 0.300 - 0.600 J/cm @Temperature -40.0 - -20.0 °C | 0.562 - 1.12 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.752 J/cm Grade Count:4 | |
| 0.588399 - 1.49492 J/cm @Temperature -30.0 - -20.0 °C | 1.10231 - 2.80060 ft-lb/in @Temperature -22.0 - -4.00 °F | Average value: 0.752 J/cm Grade Count:5 | |
| 0.588399 - 1.49492 J/cm @Thickness 3.17 - 6.40 mm | 1.10231 - 2.80060 ft-lb/in @Thickness 0.125 - 0.252 in | Average value: 0.752 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 4.81 - 12.3 J/cm | 9.00 - 22.9 ft-lb/in | Average value: 6.45 J/cm Grade Count:22 |
| Izod Impact, Notched (ISO) | 4.00 - 30.0 kJ/m2 | 1.90 - 14.3 ft-lb/in2 | Average value: 10.5 kJ/m2 Grade Count:61 |
| 3.00 - 13.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 1.43 - 6.19 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 7.73 kJ/m2 Grade Count:28 | |
| Izod Impact, Unnotched (ISO) | 10.0 - 90.0 kJ/m2 | 4.76 - 42.8 ft-lb/in2 | Average value: 58.4 kJ/m2 Grade Count:19 |
| 30.0 - 79.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 14.3 - 37.6 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 47.1 kJ/m2 Grade Count:18 | |
| Charpy Impact Unnotched | 2.00 J/cm2 - NB | 9.52 ft-lb/in2 - NB | Average value: 6.16 J/cm2 Grade Count:128 |
| 1.50 J/cm2 - NB @Temperature -40.0 - 30.0 °C | 7.14 ft-lb/in2 - NB @Temperature -40.0 - 86.0 °F | Average value: 4.87 J/cm2 Grade Count:90 | |
| Charpy Impact, Notched | 0.200 - 3.50 J/cm2 | 0.952 - 16.7 ft-lb/in2 | Average value: 1.20 J/cm2 Grade Count:140 |
| 0.150 - 7.00 J/cm2 @Temperature -40.0 - 30.0 °C | 0.714 - 33.3 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 0.793 J/cm2 Grade Count:91 | |
| Puncture Energy | 2.20 - 10.0 J | 1.62 - 7.38 ft-lb | Average value: 5.22 J Grade Count:5 |
| 2.30 - 4.00 J @Temperature -30.0 - -30.0 °C | 1.70 - 2.95 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.96 J Grade Count:4 | |
| 2.00 - 2.00 J @Temperature -30.0 - -30.0 °C | 1.48 - 1.48 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 2.96 J Grade Count:1 | |
| 2.00 - 2.00 J @Load <=55.7 kg | 1.48 - 1.48 ft-lb @Load <=123 lb | Average value: 2.96 J Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 1920 - 2680 MPa | 278000 - 389000 psi | Average value: 2170 MPa Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+17 ohm-cm | 1000 - 1.00e+17 ohm-cm | Average value: 1.18e+15 ohm-cm Grade Count:155 |
| Surface Resistance | 100 - 1.00e+16 ohm | 100 - 1.00e+16 ohm | Average value: 3.40e+14 ohm Grade Count:82 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:5 |
| Dielectric Constant | 2.60 - 19.0 | 2.60 - 19.0 | Average value: 5.58 Grade Count:62 |
| Dielectric Strength | 11.8 - 80.0 kV/mm | 300 - 2030 kV/in | Average value: 27.3 kV/mm Grade Count:101 |
| Dissipation Factor | 0.00550 - 0.380 | 0.00550 - 0.380 | Average value: 0.0775 Grade Count:55 |
| Dielectric Loss Index | 0.0250 - 0.240 | 0.0250 - 0.240 | Average value: 0.126 Grade Count:6 |
| Arc Resistance | 0.000 - 180 sec | 0.000 - 180 sec | Average value: 115 sec Grade Count:13 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 522 V Grade Count:93 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.200 - 500 μm/m-°C | 0.111 - 278 μin/in-°F | Average value: 50.8 μm/m-°C Grade Count:96 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 0.700 - 150 μm/m-°C | 0.389 - 83.3 μin/in-°F | Average value: 91.3 μm/m-°C Grade Count:39 |
| 134 - 134 μm/m-°C @Temperature 55.0 - 160 °C | 74.4 - 74.4 μin/in-°F @Temperature 131 - 320 °F | Average value: 134 μm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | Average value: 1.60 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.340 - 0.432 W/m-K | 2.36 - 3.00 BTU-in/hr-ft2-°F | Average value: 0.363 W/m-K Grade Count:12 |
| Melting Point | 210 - 262 °C | 410 - 504 °F | Average value: 220 °C Grade Count:178 |
| Maximum Service Temperature, Air | 65.0 - 200 °C | 149 - 392 °F | Average value: 141 °C Grade Count:37 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 - 252 °C | 329 - 485 °F | Average value: 212 °C Grade Count:159 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 255 °C | 131 - 491 °F | Average value: 195 °C Grade Count:248 |
| Deflection Temperature at 8.0 MPa | 50.0 - 120 °C | 122 - 248 °F | Average value: 64.6 °C Grade Count:14 |
| Vicat Softening Point | 177 - 250 °C | 351 - 482 °F | Average value: 204 °C Grade Count:70 |
| UL RTI, Electrical | 65.0 - 150 °C | 149 - 302 °F | Average value: 110 °C Grade Count:19 |
| UL RTI, Mechanical with Impact | 65.0 - 125 °C | 149 - 257 °F | Average value: 93.2 °C Grade Count:17 |
| UL RTI, Mechanical without Impact | 65.0 - 150 °C | 149 - 302 °F | Average value: 109 °C Grade Count:19 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:183 |
| Oxygen Index | 21.0 - 32.0 % | 21.0 - 32.0 % | Average value: 24.0 % Grade Count:10 |
| Glow Wire Test | 550 - 960 °C | 1020 - 1760 °F | Average value: 769 °C Grade Count:53 |
| Shrinkage | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.150 % Grade Count:3 |
| 0.0500 - 0.150 % @Temperature 120 - 120 °C | 0.0500 - 0.150 % @Temperature 248 - 248 °F | Average value: 0.100 % Grade Count:2 | |
| 0.0500 - 0.150 % @Time 14400 - 14400 sec | 0.0500 - 0.150 % @Time 4.00 - 4.00 hour | Average value: 0.100 % Grade Count:2 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 228 °C Grade Count:40 |
| Feed Temperature | 60.0 - 270 °C | 140 - 518 °F | Average value: 109 °C Grade Count:17 |
| Nozzle Temperature | 210 - 290 °C | 410 - 554 °F | Average value: 254 °C Grade Count:17 |
| Melt Temperature | 80.0 - 370 °C | 176 - 698 °F | Average value: 259 °C Grade Count:115 |
| Mold Temperature | 21.1 - 121 °C | 70.0 - 250 °F | Average value: 80.0 °C Grade Count:133 |
| Drying Temperature | 73.9 - 130 °C | 165 - 266 °F | Average value: 82.7 °C Grade Count:100 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.71 hour Grade Count:80 |
| 2.00 - 6.00 hour @Temperature 79.4 - 80.0 °C | 2.00 - 6.00 hour @Temperature 175 - 176 °F | Average value: 3.63 hour Grade Count:8 | |
| Moisture Content | 0.0300 - 2.50 % | 0.0300 - 2.50 % | Average value: 0.189 % Grade Count:69 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:7 |
| Injection Pressure | 4.96 - 172 MPa | 720 - 25000 psi | Average value: 82.3 MPa Grade Count:55 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:12 |
| Back Pressure | 0.000 - 1.38 MPa | 0.000 - 200 psi | Average value: 0.516 MPa Grade Count:9 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:3 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 62.5 rpm Grade Count:6 |