- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 3.45
- 斷裂伸長率 [%]: 16.0
- 彎曲強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 0.0127
- 硬度: 78.0
- 熱變形溫度 [℃]: 81.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 - 1.30 g/cc | 0.0365 - 0.0470 lb/in3 | Average value: 1.12 g/cc Grade Count:455 |
| Volatiles | 0.500 - 0.800 % | 0.500 - 0.800 % | Average value: 0.665 % Grade Count:17 |
| Apparent Bulk Density | 0.425 - 0.800 g/cc | 0.0154 - 0.0289 lb/in3 | Average value: 0.650 g/cc Grade Count:12 |
| Water Absorption | 0.300 - 11.0 % | 0.300 - 11.0 % | Average value: 5.00 % Grade Count:258 |
| Moisture Absorption at Equilibrium | 0.0400 - 9.50 % | 0.0400 - 9.50 % | Average value: 2.82 % Grade Count:193 |
| Water Absorption at Saturation | 6.50 - 10.0 % | 6.50 - 10.0 % | Average value: 8.98 % Grade Count:48 |
| Oxygen Transmission Rate | 40.3 cc/m2/day | 2.60 cc/100 in2/day | Average value: 40.3 cc/m2/day Grade Count:10 |
| Nitrogen Transmission | 14.0 cc-mm/m2-24hr-atm | 35.6 cc-mil/100 in2-24hr-atm | Average value: 14.0 cc-mm/m2-24hr-atm Grade Count:10 |
| Carbon Dioxide Transmission | 72.8 cc-mm/m2-24hr-atm | 185 cc-mil/100 in2-24hr-atm | Average value: 72.8 cc-mm/m2-24hr-atm Grade Count:10 |
| Viscosity | 2.60 - 50.0 cP | 2.60 - 50.0 cP | Average value: 8.83 cP Grade Count:17 |
| Viscosity Measurement | 2.19 - 260 | 2.19 - 260 | Average value: 79.0 Grade Count:81 |
| Viscosity Test | 134 - 320 cm3/g | 134 - 320 cm3/g | Average value: 189 cm3/g Grade Count:33 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:22 |
| Linear Mold Shrinkage | 0.00130 - 0.0508 cm/cm | 0.00130 - 0.0508 in/in | Average value: 0.0142 cm/cm Grade Count:243 |
| Linear Mold Shrinkage, Transverse | 0.00110 - 0.0300 cm/cm | 0.00110 - 0.0300 in/in | Average value: 0.0139 cm/cm Grade Count:49 |
| Melt Flow | 1.00 - 198 g/10 min | 1.00 - 198 g/10 min | Average value: 60.7 g/10 min Grade Count:56 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 82.0 - 88.0 | 82.0 - 88.0 | Average value: 85.0 Grade Count:5 |
| Hardness, Rockwell R | 78.0 - 122 | 78.0 - 122 | Average value: 115 Grade Count:80 |
| Hardness, Shore D | 61.0 - 85.0 | 61.0 - 85.0 | Average value: 69.7 Grade Count:22 |
| Ball Indentation Hardness | 50.0 - 190 MPa | 7250 - 27600 psi | Average value: 118 MPa Grade Count:31 |
| Tensile Strength, Ultimate | 30.0 - 110 MPa | 4350 - 16000 psi | Average value: 68.7 MPa Grade Count:159 |
| 29.0 - 80.0 MPa @Temperature -40.0 - 120 °C | 4210 - 11600 psi @Temperature -40.0 - 248 °F | Average value: 45.0 MPa Grade Count:4 | |
| 10.0 - 100 MPa @Temperature -20.0 - 100 °C | 1450 - 14500 psi @Temperature -4.00 - 212 °F | Average value: 45.0 MPa Grade Count:2 | |
| 10.0 - 100 MPa @Strain 1.00 - 8.00 % | 1450 - 14500 psi @Strain 1.00 - 8.00 % | Average value: 45.0 MPa Grade Count:2 | |
| Tensile Strength, Yield | 3.45 - 136 MPa | 500 - 19700 psi | Average value: 64.5 MPa Grade Count:258 |
| 20.0 - 142 MPa @Temperature -40.0 - 121 °C | 2900 - 20600 psi @Temperature -40.0 - 250 °F | Average value: 72.7 MPa Grade Count:14 | |
| Elongation at Break | 2.50 - 500 % | 2.50 - 500 % | Average value: 80.4 % Grade Count:340 |
| 2.50 - 2.50 % @Temperature -40.0 - -40.0 °C | 2.50 - 2.50 % @Temperature -40.0 - -40.0 °F | Average value: 2.50 % Grade Count:1 | |
| Elongation at Yield | 3.00 - 140 % | 3.00 - 140 % | Average value: 14.7 % Grade Count:142 |
| 3.00 - 42.0 % @Temperature -40.0 - 121 °C | 3.00 - 42.0 % @Temperature -40.0 - 250 °F | Average value: 34.3 % Grade Count:5 | |
| Modulus of Elasticity | 0.350 - 4.00 GPa | 50.8 - 580 ksi | Average value: 2.25 GPa Grade Count:188 |
| 0.360 - 3.75 GPa @Temperature -40.0 - 120 °C | 52.2 - 544 ksi @Temperature -40.0 - 248 °F | Average value: 1.69 GPa Grade Count:4 | |
| Flexural Yield Strength | 16.0 - 160 MPa | 2320 - 23200 psi | Average value: 82.6 MPa Grade Count:246 |
| 8.00 - 183 MPa @Temperature -40.0 - 250 °C | 1160 - 26500 psi @Temperature -40.0 - 482 °F | Average value: 86.7 MPa Grade Count:16 | |
| Flexural Modulus | 0.0127 - 3.65 GPa | 1.85 - 530 ksi | Average value: 2.09 GPa Grade Count:280 |
| 0.260 - 3.90 GPa @Temperature -40.0 - 121 °C | 37.7 - 566 ksi @Temperature -40.0 - 250 °F | Average value: 1.29 GPa Grade Count:14 | |
| Compressive Yield Strength | 6.00 - 96.5 MPa | 870 - 14000 psi | Average value: 48.0 MPa Grade Count:7 |
| Poissons Ratio | 0.350 - 0.450 | 0.350 - 0.450 | Average value: 0.372 Grade Count:5 |
| Izod Impact, Notched | 0.200 J/cm - NB | 0.375 ft-lb/in - NB | Average value: 1.43 J/cm Grade Count:204 |
| 0.210 - 2.10 J/cm @Temperature -40.0 - -20.0 °C | 0.393 - 3.93 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.784 J/cm Grade Count:19 | |
| 0.534 - 2.54973 J/cm @Temperature -40.0 - -30.0 °C | 1.00 - 4.77669 ft-lb/in @Temperature -40.0 - -22.0 °F | Average value: 0.784 J/cm Grade Count:4 | |
| 0.534 - 2.54973 J/cm @Thickness 1.57 - 6.40 mm | 1.00 - 4.77669 ft-lb/in @Thickness 0.0618 - 0.252 in | Average value: 0.784 J/cm Grade Count:4 | |
| Izod Impact, Unnotched | 5.34 J/cm - NB | 10.0 ft-lb/in - NB | Average value: 9.08 J/cm Grade Count:7 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 - NB | 1.90 ft-lb/in2 - NB | Average value: 32.7 kJ/m2 Grade Count:61 |
| 3.00 kJ/m2 - NB @Temperature -40.0 - -20.0 °C | 1.43 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 12.6 kJ/m2 Grade Count:19 | |
| Izod Impact, Unnotched (ISO) | 96.0 kJ/m2 - NB | 45.7 ft-lb/in2 - NB | Average value: 97.0 kJ/m2 Grade Count:5 |
| 200 kJ/m2 - NB @Temperature -30.0 - -30.0 °C | 95.2 ft-lb/in2 - NB @Temperature -22.0 - -22.0 °F | Average value: 200 kJ/m2 Grade Count:4 | |
| Charpy Impact Unnotched | 4.00 J/cm2 - NB | 19.0 ft-lb/in2 - NB | Average value: 11.5 J/cm2 Grade Count:140 |
| 3.00 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 14.3 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 10.2 J/cm2 Grade Count:86 | |
| Charpy Impact, Notched | 0.110 J/cm2 - NB | 0.524 ft-lb/in2 - NB | Average value: 2.38 J/cm2 Grade Count:150 |
| 0.150 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 0.714 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 0.955 J/cm2 Grade Count:81 | |
| Dart Drop, Total Energy | 67.8 - 285 J | 50.0 - 210 ft-lb | Average value: 204 J Grade Count:4 |
| Puncture Energy | 12.0 - 165 J | 8.85 - 122 ft-lb | Average value: 98.1 J Grade Count:8 |
| 10.0 - 160 J @Temperature -30.0 - -30.0 °C | 7.38 - 118 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 67.6 J Grade Count:8 | |
| Coefficient of Friction | 0.240 - 0.420 | 0.240 - 0.420 | Average value: 0.344 Grade Count:5 |
| Tensile Creep Modulus, 1 hour | 700 - 3700 MPa | 102000 - 537000 psi | Average value: 1820 MPa Grade Count:11 |
| Tensile Creep Modulus, 1000 hours | 550 - 2300 MPa | 79800 - 334000 psi | Average value: 985 MPa Grade Count:15 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+17 ohm-cm | 1000 - 1.00e+17 ohm-cm | Average value: 1.19e+15 ohm-cm Grade Count:160 |
| Surface Resistance | 1.00e+6 - 1.00e+16 ohm | 1.00e+6 - 1.00e+16 ohm | Average value: 3.17e+14 ohm Grade Count:92 |
| Dielectric Constant | 2.50 - 20.0 | 2.50 - 20.0 | Average value: 4.79 Grade Count:97 |
| Dielectric Strength | 15.7 - 100 kV/mm | 400 - 2540 kV/in | Average value: 30.2 kV/mm Grade Count:98 |
| Dissipation Factor | 0.00500 - 0.390 | 0.00500 - 0.390 | Average value: 0.0716 Grade Count:71 |
| Dielectric Loss Index | 0.0200 - 0.300 | 0.0200 - 0.300 | Average value: 0.138 Grade Count:15 |
| Arc Resistance | 60.0 - 195 sec | 60.0 - 195 sec | Average value: 140 sec Grade Count:20 |
| Comparative Tracking Index | 450 - 600 V | 450 - 600 V | Average value: 596 V Grade Count:103 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.600 - 200 μm/m-°C | 0.333 - 111 μin/in-°F | Average value: 78.5 μm/m-°C Grade Count:107 |
| 170 - 170 μm/m-°C @Temperature 50.0 - 160 °C | 94.4 - 94.4 μin/in-°F @Temperature 122 - 320 °F | Average value: 170 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 78.0 - 190 μm/m-°C | 43.3 - 106 μin/in-°F | Average value: 115 μm/m-°C Grade Count:35 |
| Specific Heat Capacity | 1.50 - 1.70 J/g-°C | 0.359 - 0.406 BTU/lb-°F | Average value: 1.62 J/g-°C Grade Count:13 |
| Thermal Conductivity | 0.230 - 0.330 W/m-K | 1.60 - 2.29 BTU-in/hr-ft2-°F | Average value: 0.286 W/m-K Grade Count:21 |
| Melting Point | 141 - 295 °C | 286 - 563 °F | Average value: 220 °C Grade Count:369 |
| Maximum Service Temperature, Air | 80.0 - 250 °C | 176 - 482 °F | Average value: 122 °C Grade Count:44 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 - 200 °C | 178 - 392 °F | Average value: 168 °C Grade Count:186 |
| Deflection Temperature at 1.8 MPa (264 psi) | 32.2 - 110 °C | 90.0 - 230 °F | Average value: 63.5 °C Grade Count:287 |
| Deflection Temperature at 8.0 MPa | 40.0 - 50.0 °C | 104 - 122 °F | Average value: 45.0 °C Grade Count:8 |
| Vicat Softening Point | 60.0 - 204 °C | 140 - 399 °F | Average value: 183 °C Grade Count:67 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:4 |
| Glass Transition Temp, Tg | 60.0 - 142 °C | 140 - 288 °F | Average value: 111 °C Grade Count:4 |
| Decomposition Temperature | 300 - 350 °C | 572 - 662 °F | Average value: 306 °C Grade Count:16 |
| UL RTI, Electrical | 65.0 - 130 °C | 149 - 266 °F | Average value: 78.1 °C Grade Count:7 |
| UL RTI, Mechanical with Impact | 65.0 - 105 °C | 149 - 221 °F | Average value: 73.1 °C Grade Count:7 |
| UL RTI, Mechanical without Impact | 65.0 - 105 °C | 149 - 221 °F | Average value: 74.4 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:147 |
| Flammability Test | 13.0 - 165 | 13.0 - 165 | Average value: 65.0 Grade Count:3 |
| Oxygen Index | 21.0 - 28.0 % | 21.0 - 28.0 % | Average value: 24.5 % Grade Count:21 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 773 °C Grade Count:17 |
| Shrinkage | 0.200 - 0.210 % @Temperature 120 - 120 °C | 0.200 - 0.210 % @Temperature 248 - 248 °F | Average value: 0.205 % Grade Count:1 |
| 0.200 - 0.210 % @Time 14400 - 14400 sec | 0.200 - 0.210 % @Time 4.00 - 4.00 hour | Average value: 0.205 % Grade Count:1 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 335 °C | 176 - 635 °F | Average value: 243 °C Grade Count:42 |
| Feed Temperature | 60.0 - 230 °C | 140 - 446 °F | Average value: 109 °C Grade Count:4 |
| Nozzle Temperature | 210 - 271 °C | 410 - 520 °F | Average value: 246 °C Grade Count:32 |
| Die Temperature | 230 - 245 °C | 446 - 473 °F | Average value: 238 °C Grade Count:4 |
| Melt Temperature | 80.0 - 330 °C | 176 - 626 °F | Average value: 242 °C Grade Count:171 |
| Mold Temperature | 21.1 - 120 °C | 70.0 - 248 °F | Average value: 71.7 °C Grade Count:142 |
| Drying Temperature | 65.0 - 130 °C | 149 - 266 °F | Average value: 82.1 °C Grade Count:105 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 3.65 hour Grade Count:87 |
| 2.00 - 6.00 hour @Temperature 80.0 - 80.0 °C | 2.00 - 6.00 hour @Temperature 176 - 176 °F | Average value: 4.00 hour Grade Count:2 | |
| Moisture Content | 0.000 - 2.50 % | 0.000 - 2.50 % | Average value: 0.198 % Grade Count:91 |
| Injection Pressure | 3.45 - 172 MPa | 500 - 25000 psi | Average value: 88.6 MPa Grade Count:29 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 2.95 MPa Grade Count:17 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 70.2 rpm Grade Count:14 |