- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.0
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 |
| Filler Content | 30 % | 30 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 6.0 % | 6.0 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Strength | 270 MPa | 39200 psi | 23°C, at break; ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A |
| 14.0 kJ/m2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |
| Charpy Impact Unnotched | 7.50 J/cm2 @Temperature -30.0 °C | 35.7 ft-lb/in2 @Temperature -22.0 °F | ISO 179/eU |
| 8.50 J/cm2 @Temperature 23.0 °C | 40.5 ft-lb/in2 @Temperature 73.4 °F | ISO 179/eU | |
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/eA |
| 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1/2 |
| Vicat Softening Point | 255 °C | 491 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Glow Wire Test | 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | plaque; IEC 60695 |