- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.932
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.3
- 拉伸強度 [MPa]: 36.0
- 斷裂伸長率 [%]: 25.0
- 彎曲強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.0126
- 硬度: 97.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 - 1.62 g/cc | 0.0337 - 0.0585 lb/in3 | Average value: 1.18 g/cc Grade Count:95 |
| Water Absorption | 0.0600 - 9.50 % | 0.0600 - 9.50 % | Average value: 3.67 % Grade Count:49 |
| Moisture Absorption at Equilibrium | 0.170 - 3.50 % | 0.170 - 3.50 % | Average value: 2.34 % Grade Count:32 |
| Viscosity | 2.60 cP | 2.60 cP | Average value: 2.60 cP Grade Count:12 |
| Viscosity Measurement | 0.870 - 48.0 | 0.870 - 48.0 | Average value: 28.7 Grade Count:17 |
| Maximum Moisture Content | 0.100 | 0.100 | Average value: 0.100 Grade Count:4 |
| Linear Mold Shrinkage | 0.000400 - 0.0190 cm/cm | 0.000400 - 0.0190 in/in | Average value: 0.0117 cm/cm Grade Count:74 |
| Linear Mold Shrinkage, Transverse | 0.000400 - 0.0160 cm/cm | 0.000400 - 0.0160 in/in | Average value: 0.0104 cm/cm Grade Count:24 |
| Melt Flow | 8.00 - 160 g/10 min | 8.00 - 160 g/10 min | Average value: 41.0 g/10 min Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97.0 - 121 | 97.0 - 121 | Average value: 115 Grade Count:33 |
| Hardness, Shore D | 71.0 - 92.0 | 71.0 - 92.0 | Average value: 78.4 Grade Count:7 |
| Ball Indentation Hardness | 70.0 - 150 MPa | 10200 - 21800 psi | Average value: 112 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 17.0 - 157 MPa | 2470 - 22800 psi | Average value: 71.0 MPa Grade Count:62 |
| 20.0 - 130 MPa @Temperature -40.0 - 120 °C | 2900 - 18900 psi @Temperature -40.0 - 248 °F | Average value: 59.8 MPa Grade Count:9 | |
| Tensile Strength, Yield | 36.0 - 90.0 MPa | 5220 - 13100 psi | Average value: 64.8 MPa Grade Count:42 |
| 20.0 - 142 MPa @Temperature -40.0 - 120 °C | 2900 - 20600 psi @Temperature -40.0 - 248 °F | Average value: 62.5 MPa Grade Count:8 | |
| Elongation at Break | 2.50 - 200 % | 2.50 - 200 % | Average value: 38.0 % Grade Count:83 |
| 2.50 - 5.00 % @Temperature -40.0 - 120 °C | 2.50 - 5.00 % @Temperature -40.0 - 248 °F | Average value: 51.8 % Grade Count:6 | |
| Elongation at Yield | 3.00 - 28.0 % | 3.00 - 28.0 % | Average value: 9.79 % Grade Count:27 |
| 3.00 - 42.0 % @Temperature -40.0 - 120 °C | 3.00 - 42.0 % @Temperature -40.0 - 248 °F | Average value: 26.6 % Grade Count:8 | |
| Modulus of Elasticity | 0.970 - 4.00 GPa | 141 - 580 ksi | Average value: 2.82 GPa Grade Count:54 |
| 0.320 - 4.09 GPa @Temperature -40.0 - 120 °C | 46.4 - 593 ksi @Temperature -40.0 - 248 °F | Average value: 1.39 GPa Grade Count:6 | |
| Flexural Yield Strength | 25.0 - 900 MPa | 3630 - 131000 psi | Average value: 101 MPa Grade Count:72 |
| 17.0 - 183 MPa @Temperature -40.0 - 120 °C | 2470 - 26500 psi @Temperature -40.0 - 248 °F | Average value: 85.1 MPa Grade Count:12 | |
| Flexural Modulus | 0.0126 - 3.50 GPa | 1.82 - 508 ksi | Average value: 2.41 GPa Grade Count:73 |
| 0.305 - 5.50 GPa @Temperature -40.0 - 120 °C | 44.2 - 798 ksi @Temperature -40.0 - 248 °F | Average value: 1.40 GPa Grade Count:8 | |
| Compressive Yield Strength | 62.0 - 85.0 MPa | 8990 - 12300 psi | Average value: 74.2 MPa Grade Count:5 |
| Izod Impact, Notched | 0.300 J/cm - NB | 0.562 ft-lb/in - NB | Average value: 1.04 J/cm Grade Count:46 |
| 0.210 - 0.500 J/cm @Temperature -40.0 - -40.0 °C | 0.393 - 0.937 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.374 J/cm Grade Count:11 | |
| Izod Impact, Unnotched | 4.81 - 5340 J/cm | 9.00 - 10000 ft-lb/in | Average value: 7.74 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 3.00 - 10.0 kJ/m2 | 1.43 - 4.76 ft-lb/in2 | Average value: 6.17 kJ/m2 Grade Count:16 |
| 3.00 - 10.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 1.43 - 4.76 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 5.86 kJ/m2 Grade Count:7 | |
| Izod Impact, Unnotched (ISO) | 100 - 100 kJ/m2 @Temperature -30.0 - -30.0 °C | 47.6 - 47.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 100 kJ/m2 Grade Count:1 |
| Charpy Impact Unnotched | 0.400 J/cm2 - NB | 1.90 ft-lb/in2 - NB | Average value: 8.44 J/cm2 Grade Count:36 |
| 5.00 - 999.9 J/cm2 @Temperature -30.0 - -20.0 °C | 23.8 - 4759 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 9.51 J/cm2 Grade Count:19 | |
| Charpy Impact, Notched | 0.200 - 6.00 J/cm2 | 0.952 - 28.6 ft-lb/in2 | Average value: 0.751 J/cm2 Grade Count:41 |
| 0.200 - 1.00 J/cm2 @Temperature -30.0 - -20.0 °C | 0.952 - 4.76 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.352 J/cm2 Grade Count:20 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.00e+17 ohm-cm | 1.00e+8 - 1.00e+17 ohm-cm | Average value: 1.78e+15 ohm-cm Grade Count:58 |
| Surface Resistance | 1.00e+10 - 1.00e+16 ohm | 1.00e+10 - 1.00e+16 ohm | Average value: 3.57e+14 ohm Grade Count:36 |
| Dielectric Constant | 3.10 - 8.00 | 3.10 - 8.00 | Average value: 4.30 Grade Count:17 |
| Dielectric Strength | 12.0 - 100 kV/mm | 305 - 2540 kV/in | Average value: 25.3 kV/mm Grade Count:45 |
| Dissipation Factor | 0.00900 - 0.125 | 0.00900 - 0.125 | Average value: 0.0316 Grade Count:10 |
| Arc Resistance | 60.0 - 125 sec | 60.0 - 125 sec | Average value: 112 sec Grade Count:6 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 553 V Grade Count:43 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 59.4 - 99.0 μm/m-°C | 33.0 - 55.0 μin/in-°F | Average value: 75.5 μm/m-°C Grade Count:25 |
| Specific Heat Capacity | 3.73 J/g-°C | 0.891 BTU/lb-°F | Average value: 3.73 J/g-°C Grade Count:4 |
| Thermal Conductivity | 0.230 - 0.264 W/m-K | 1.60 - 1.83 BTU-in/hr-ft2-°F | Average value: 0.257 W/m-K Grade Count:5 |
| Melting Point | 215 - 225 °C | 419 - 437 °F | Average value: 220 °C Grade Count:61 |
| Maximum Service Temperature, Air | 90.0 - 180 °C | 194 - 356 °F | Average value: 125 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 - 210 °C | 302 - 410 °F | Average value: 182 °C Grade Count:44 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 215 °C | 122 - 419 °F | Average value: 71.5 °C Grade Count:79 |
| Vicat Softening Point | 182 - 225 °C | 360 - 437 °F | Average value: 201 °C Grade Count:32 |
| UL RTI, Electrical | 125 - 130 °C | 257 - 266 °F | Average value: 127 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 75.0 - 105 °C | 167 - 221 °F | Average value: 85.0 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 110 - 125 °C | 230 - 257 °F | Average value: 119 °C Grade Count:3 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:84 |
| Oxygen Index | 25.0 - 40.0 % | 25.0 - 40.0 % | Average value: 31.1 % Grade Count:7 |
| Glow Wire Test | 775 - 960 °C | 1430 - 1760 °F | Average value: 915 °C Grade Count:34 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 271 °C | 430 - 520 °F | Average value: 243 °C Grade Count:11 |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Average value: 70.0 °C Grade Count:6 |
| Nozzle Temperature | 210 - 266 °C | 410 - 510 °F | Average value: 242 °C Grade Count:12 |
| Melt Temperature | 80.0 - 300 °C | 176 - 572 °F | Average value: 241 °C Grade Count:52 |
| Mold Temperature | 30.0 - 120 °C | 86.0 - 248 °F | Average value: 72.5 °C Grade Count:46 |
| Drying Temperature | 75.0 - 130 °C | 167 - 266 °F | Average value: 82.7 °C Grade Count:39 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.62 hour Grade Count:29 |
| 2.00 - 4.00 hour @Temperature 71.1 - 71.1 °C | 2.00 - 4.00 hour @Temperature 160 - 160 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0300 - 2.50 % | 0.0300 - 2.50 % | Average value: 0.334 % Grade Count:26 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 4.96 - 130 MPa | 720 - 18900 psi | Average value: 76.0 MPa Grade Count:26 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:4 |