- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 138.0
- 斷裂伸長率 [%]: 75.0
- 彎曲強度 [MPa]: 70.0
- 彎曲模量 [MPa]: 6.21
- 硬度: 114.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.53 g/cc | 0.0401 - 0.0553 lb/in3 | Average value: 1.27 g/cc Grade Count:52 |
| Filler Content | 1.00 - 40.0 % | 1.00 - 40.0 % | Average value: 17.6 % Grade Count:11 |
| Water Absorption | 0.300 - 1.50 % | 0.300 - 1.50 % | Average value: 0.979 % Grade Count:31 |
| Moisture Absorption at Equilibrium | 1.80 - 2.50 % | 1.80 - 2.50 % | Average value: 2.18 % Grade Count:6 |
| Additive Loading | 20.0 - 40.0 % | 20.0 - 40.0 % | Average value: 30.0 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000200 - 0.0350 cm/cm | 0.000200 - 0.0350 in/in | Average value: 0.00387 cm/cm Grade Count:47 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00100 - 0.00400 cm/cm | 0.00100 - 0.00400 in/in | Average value: 0.00240 cm/cm Grade Count:5 |
| Linear Mold Shrinkage, Transverse | 0.00590 - 0.0140 cm/cm | 0.00590 - 0.0140 in/in | Average value: 0.00968 cm/cm Grade Count:10 |
| Melt Flow | 3.00 - 60.0 g/10 min | 3.00 - 60.0 g/10 min | Average value: 25.9 g/10 min Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 - 212 | 114 - 212 | Average value: 123 Grade Count:14 |
| Ball Indentation Hardness | 90.0 - 270 MPa | 13100 - 39200 psi | Average value: 191 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 70.0 - 234 MPa | 10200 - 34000 psi | Average value: 160 MPa Grade Count:42 |
| Tensile Strength, Yield | 138 - 221 MPa | 20000 - 32000 psi | Average value: 188 MPa Grade Count:9 |
| Elongation at Break | 1.00 - 20.0 % | 1.00 - 20.0 % | Average value: 3.47 % Grade Count:35 |
| Elongation at Yield | 1.00 - 4.50 % | 1.00 - 4.50 % | Average value: 2.58 % Grade Count:14 |
| Modulus of Elasticity | 4.00 - 32.4 GPa | 580 - 4700 ksi | Average value: 13.6 GPa Grade Count:41 |
| Flexural Yield Strength | 75.0 - 345 MPa | 10900 - 50000 psi | Average value: 246 MPa Grade Count:43 |
| Flexural Modulus | 6.21 - 21.4 GPa | 900 - 3100 ksi | Average value: 12.5 GPa Grade Count:40 |
| Izod Impact, Notched | 0.427 - 2.08 J/cm | 0.800 - 3.90 ft-lb/in | Average value: 0.945 J/cm Grade Count:23 |
| 1.01441 - 1.01441 J/cm @Temperature -40.0 - -40.0 °C | 1.90041 - 1.90041 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.01 J/cm Grade Count:1 | |
| 1.01441 - 1.01441 J/cm @Thickness 3.17 - 3.17 mm | 1.90041 - 1.90041 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.01 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 4.27 - 17.1 J/cm | 8.00 - 32.0 ft-lb/in | Average value: 8.86 J/cm Grade Count:15 |
| Charpy Impact Unnotched | 1.70 J/cm2 - NB | 8.09 ft-lb/in2 - NB | Average value: 5.09 J/cm2 Grade Count:28 |
| 4.00 - 6.00 J/cm2 @Temperature -30.0 - -20.0 °C | 19.0 - 28.6 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 4.87 J/cm2 Grade Count:6 | |
| Charpy Impact, Notched | 0.300 - 1.80 J/cm2 | 1.43 - 8.57 ft-lb/in2 | Average value: 0.932 J/cm2 Grade Count:18 |
| 0.400 - 1.50 J/cm2 @Temperature -30.0 - -20.0 °C | 1.90 - 7.14 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.800 J/cm2 Grade Count:3 | |
| Puncture Energy | 1.70 - 1.70 J @Temperature -30.0 - -30.0 °C | 1.25 - 1.25 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.70 J Grade Count:1 |
| Coefficient of Friction | 0.150 - 0.240 | 0.150 - 0.240 | Average value: 0.208 Grade Count:5 |
| Coefficient of Friction, Static | 0.140 - 0.210 | 0.140 - 0.210 | Average value: 0.180 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 2.00e+13 ohm-cm | 1.00 - 2.00e+13 ohm-cm | Average value: 1.05e+12 ohm-cm Grade Count:19 |
| Surface Resistance | 0.190 - 6.00e+12 ohm | 0.190 - 6.00e+12 ohm | Average value: 2.22e+11 ohm Grade Count:27 |
| Insulation Resistance | 100 - 1.00e+9 ohm | 100 - 1.00e+9 ohm | Average value: 2.86e+8 ohm Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 - 80.0 μm/m-°C | 8.00 - 44.4 μin/in-°F | Average value: 26.6 μm/m-°C Grade Count:20 |
| Thermal Conductivity | 0.300 - 0.500 W/m-K | 2.08 - 3.47 BTU-in/hr-ft2-°F | Average value: 0.385 W/m-K Grade Count:6 |
| Melting Point | 215 - 221 °C | 419 - 430 °F | Average value: 219 °C Grade Count:17 |
| Maximum Service Temperature, Air | 90.0 - 250 °C | 194 - 482 °F | Average value: 133 °C Grade Count:15 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 260 °C | 410 - 500 °F | Average value: 219 °C Grade Count:15 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 - 249 °C | 338 - 480 °F | Average value: 204 °C Grade Count:33 |
| Vicat Softening Point | 165 - 220 °C | 329 - 428 °F | Average value: 208 °C Grade Count:17 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:24 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 330 °C | 430 - 626 °F | Average value: 276 °C Grade Count:19 |
| Nozzle Temperature | 270 - 340 °C | 518 - 644 °F | Average value: 292 °C Grade Count:14 |
| Melt Temperature | 230 - 340 °C | 446 - 644 °F | Average value: 283 °C Grade Count:32 |
| Mold Temperature | 54.4 - 120 °C | 130 - 248 °F | Average value: 85.8 °C Grade Count:37 |
| Drying Temperature | 75.0 - 110 °C | 167 - 230 °F | Average value: 89.3 °C Grade Count:26 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 2.50 hour Grade Count:4 |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.154 % Grade Count:12 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:6 |
| Injection Pressure | 68.9 - 130 MPa | 10000 - 18900 psi | Average value: 92.2 MPa Grade Count:17 |