- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 0.28
- 拉伸強度 [MPa]: 30.0
- 斷裂伸長率 [%]: 73.6
- 彎曲強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 2.30
- 硬度: 110.0
- 熱變形溫度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 - 1.82 g/cc | 0.0430 - 0.0658 lb/in3 | Average value: 1.46 g/cc Grade Count:112 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 24.3 % Grade Count:23 |
| Water Absorption | 0.600 - 6.70 % | 0.600 - 6.70 % | Average value: 1.87 % Grade Count:26 |
| Moisture Absorption at Equilibrium | 0.170 - 4.00 % | 0.170 - 4.00 % | Average value: 1.50 % Grade Count:15 |
| Viscosity Measurement | 0.400 - 50.0 | 0.400 - 50.0 | Average value: 8.36 Grade Count:13 |
| Viscosity Test | 104 - 150 cm3/g | 104 - 150 cm3/g | Average value: 135 cm3/g Grade Count:4 |
| Linear Mold Shrinkage | 0.000800 - 0.0150 cm/cm | 0.000800 - 0.0150 in/in | Average value: 0.00450 cm/cm Grade Count:96 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00414 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0158 cm/cm | 0.00100 - 0.0158 in/in | Average value: 0.00856 cm/cm Grade Count:44 |
| Melt Flow | 1.00 - 55.0 g/10 min | 1.00 - 55.0 g/10 min | Average value: 13.8 g/10 min Grade Count:33 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 121 | 110 - 121 | Average value: 118 Grade Count:19 |
| Hardness, Shore D | 80.0 - 90.0 | 80.0 - 90.0 | Average value: 86.3 Grade Count:6 |
| Ball Indentation Hardness | 120 - 370 MPa | 17400 - 53700 psi | Average value: 203 MPa Grade Count:9 |
| Tensile Strength, Ultimate | 30.0 - 210 MPa | 4350 - 30500 psi | Average value: 116 MPa Grade Count:106 |
| Tensile Strength, Yield | 30.0 - 210 MPa | 4350 - 30500 psi | Average value: 110 MPa Grade Count:11 |
| Elongation at Break | 1.50 - 70.0 % | 1.50 - 70.0 % | Average value: 4.42 % Grade Count:106 |
| Elongation at Yield | 2.00 - 9.70 % | 2.00 - 9.70 % | Average value: 3.88 % Grade Count:10 |
| Modulus of Elasticity | 1.00 - 17.9 GPa | 145 - 2600 ksi | Average value: 8.29 GPa Grade Count:74 |
| Flexural Yield Strength | 73.6 - 283 MPa | 10700 - 41000 psi | Average value: 182 MPa Grade Count:82 |
| Flexural Modulus | 2.30 - 15.9 GPa | 334 - 2300 ksi | Average value: 7.25 GPa Grade Count:83 |
| Compressive Yield Strength | 75.8 - 103 MPa | 11000 - 15000 psi | Average value: 94.8 MPa Grade Count:4 |
| Izod Impact, Notched | 0.280 - 1.80 J/cm | 0.525 - 3.37 ft-lb/in | Average value: 0.935 J/cm Grade Count:45 |
| Izod Impact, Unnotched | 4.81 - 10.7 J/cm | 9.00 - 20.0 ft-lb/in | Average value: 7.31 J/cm Grade Count:19 |
| Izod Impact, Notched (ISO) | 2.50 - 107 kJ/m2 | 1.19 - 50.9 ft-lb/in2 | Average value: 12.0 kJ/m2 Grade Count:22 |
| 6.00 - 10.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 2.86 - 4.76 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 8.30 kJ/m2 Grade Count:9 | |
| Izod Impact, Unnotched (ISO) | 10.0 - 68.0 kJ/m2 | 4.76 - 32.4 ft-lb/in2 | Average value: 50.0 kJ/m2 Grade Count:9 |
| 35.0 - 67.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 16.7 - 31.9 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 52.8 kJ/m2 Grade Count:5 | |
| Charpy Impact Unnotched | 1.50 - 13.5 J/cm2 | 7.14 - 64.2 ft-lb/in2 | Average value: 5.28 J/cm2 Grade Count:48 |
| 1.50 - 7.90 J/cm2 @Temperature -30.0 - -20.0 °C | 7.14 - 37.6 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 4.34 J/cm2 Grade Count:24 | |
| Charpy Impact, Notched | 0.100 - 1.80 J/cm2 | 0.476 - 8.57 ft-lb/in2 | Average value: 0.750 J/cm2 Grade Count:48 |
| 0.100 - 1.00 J/cm2 @Temperature -30.0 - -20.0 °C | 0.476 - 4.76 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.577 J/cm2 Grade Count:27 | |
| Puncture Energy | 1.90 - 1.90 J @Temperature -30.0 - -30.0 °C | 1.40 - 1.40 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.90 J Grade Count:1 |
| 1.90 - 1.90 J @Load <=91.8 kg | 1.40 - 1.40 ft-lb @Load <=202 lb | Average value: 1.90 J Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+17 ohm-cm | 1.00e+12 - 1.00e+17 ohm-cm | Average value: 6.14e+15 ohm-cm Grade Count:50 |
| Surface Resistance | 1.00e+10 - 8.00e+15 ohm | 1.00e+10 - 8.00e+15 ohm | Average value: 7.93e+14 ohm Grade Count:35 |
| Dielectric Constant | 2.90 - 4.35 | 2.90 - 4.35 | Average value: 3.86 Grade Count:16 |
| Dielectric Strength | 11.0 - 70.0 kV/mm | 280 - 1780 kV/in | Average value: 28.6 kV/mm Grade Count:51 |
| Dissipation Factor | 0.0130 - 0.0800 | 0.0130 - 0.0800 | Average value: 0.0230 Grade Count:12 |
| Comparative Tracking Index | 225 - 600 V | 225 - 600 V | Average value: 475 V Grade Count:50 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 82.0 μm/m-°C | 11.1 - 45.6 μin/in-°F | Average value: 49.8 μm/m-°C Grade Count:16 |
| CTE, linear, Transverse to Flow | 23.0 - 90.0 μm/m-°C | 12.8 - 50.0 μin/in-°F | Average value: 64.8 μm/m-°C Grade Count:6 |
| Thermal Conductivity | 0.303 - 0.331 W/m-K | 2.10 - 2.30 BTU-in/hr-ft2-°F | Average value: 0.321 W/m-K Grade Count:4 |
| Melting Point | 215 - 225 °C | 419 - 437 °F | Average value: 221 °C Grade Count:61 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 - 245 °C | 329 - 473 °F | Average value: 209 °C Grade Count:46 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 230 °C | 158 - 446 °F | Average value: 191 °C Grade Count:94 |
| Vicat Softening Point | 195 - 250 °C | 383 - 482 °F | Average value: 208 °C Grade Count:45 |
| UL RTI, Electrical | 65.0 - 130 °C | 149 - 266 °F | Average value: 96.3 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 92.5 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 92.5 °C Grade Count:4 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:109 |
| Oxygen Index | 22.0 - 35.0 % | 22.0 - 35.0 % | Average value: 28.1 % Grade Count:11 |
| Glow Wire Test | 600 - 960 °C | 1110 - 1760 °F | Average value: 914 °C Grade Count:54 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 300 °C | 430 - 572 °F | Average value: 251 °C Grade Count:19 |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Average value: 70.0 °C Grade Count:8 |
| Nozzle Temperature | 210 - 268 °C | 410 - 515 °F | Average value: 246 °C Grade Count:11 |
| Melt Temperature | 210 - 300 °C | 410 - 572 °F | Average value: 251 °C Grade Count:66 |
| Mold Temperature | 30.0 - 120 °C | 86.0 - 248 °F | Average value: 74.5 °C Grade Count:74 |
| Drying Temperature | 75.0 - 130 °C | 167 - 266 °F | Average value: 84.5 °C Grade Count:68 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.34 hour Grade Count:43 |
| Moisture Content | 0.0300 - 2.00 % | 0.0300 - 2.00 % | Average value: 0.189 % Grade Count:55 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:11 |
| Injection Pressure | 3.45 - 138 MPa | 500 - 20000 psi | Average value: 87.8 MPa Grade Count:55 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | Average value: 75.0 MPa Grade Count:6 |
| Screw Speed | 50.0 - 200 rpm | 50.0 - 200 rpm | Average value: 102 rpm Grade Count:3 |