- 熔體流動速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 60.0
- 斷裂伸長率 [%]: 40.7
- 彎曲強度 [MPa]: 44.8
- 彎曲模量 [MPa]: 0.993
- 硬度: 100.0
- 熱變形溫度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.47 g/cc | 0.0408 - 0.0531 lb/in3 | Average value: 1.17 g/cc Grade Count:34 |
| Water Absorption | 0.200 - 3.20 % | 0.200 - 3.20 % | Average value: 1.22 % Grade Count:12 |
| Moisture Absorption at Equilibrium | 2.20 - 3.00 % | 2.20 - 3.00 % | Average value: 2.40 % Grade Count:10 |
| Water Absorption at Saturation | 6.00 - 10.0 % | 6.00 - 10.0 % | Average value: 6.98 % Grade Count:14 |
| Linear Mold Shrinkage | 0.00100 - 0.0250 cm/cm | 0.00100 - 0.0250 in/in | Average value: 0.0116 cm/cm Grade Count:14 |
| Linear Mold Shrinkage, Transverse | 0.00950 - 0.0180 cm/cm | 0.00950 - 0.0180 in/in | Average value: 0.0126 cm/cm Grade Count:4 |
| Melt Flow | 15.0 - 100 g/10 min | 15.0 - 100 g/10 min | Average value: 61.0 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80.0 - 84.0 | 80.0 - 84.0 | Average value: 81.5 Grade Count:4 |
| Hardness, Rockwell R | 100 - 120 | 100 - 120 | Average value: 112 Grade Count:4 |
| Hardness, Shore D | 78.0 - 85.0 | 78.0 - 85.0 | Average value: 82.7 Grade Count:7 |
| Ball Indentation Hardness | 130 - 210 MPa | 18900 - 30500 psi | Average value: 158 MPa Grade Count:14 |
| Tensile Strength, Ultimate | 44.8 - 160 MPa | 6500 - 23200 psi | Average value: 87.1 MPa Grade Count:21 |
| 33.0 - 50.0 MPa @Temperature 60.0 - 120 °C | 4790 - 7250 psi @Temperature 140 - 248 °F | Average value: 41.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 60.0 - 110 MPa | 8700 - 16000 psi | Average value: 82.7 MPa Grade Count:13 |
| Elongation at Break | 4.00 - 60.0 % | 4.00 - 60.0 % | Average value: 20.3 % Grade Count:25 |
| Creep Strength | 6.00 - 20.0 MPa | 870 - 2900 psi | Average value: 12.3 MPa Grade Count:6 |
| Modulus of Elasticity | 1.20 - 9.50 GPa | 174 - 1380 ksi | Average value: 3.85 GPa Grade Count:28 |
| 0.500 - 0.900 GPa @Temperature 100 - 100 °C | 72.5 - 131 ksi @Temperature 212 - 212 °F | Average value: 0.700 GPa Grade Count:2 | |
| Flexural Yield Strength | 40.7 - 240 MPa | 5900 - 34800 psi | Average value: 112 MPa Grade Count:28 |
| Flexural Modulus | 0.993 - 3.70 GPa | 144 - 537 ksi | Average value: 2.95 GPa Grade Count:26 |
| 0.680 - 1.60 GPa @Temperature 60.0 - 120 °C | 98.6 - 232 ksi @Temperature 140 - 248 °F | Average value: 1.13 GPa Grade Count:1 | |
| Compressive Yield Strength | 33.0 - 145 MPa | 4790 - 21000 psi | Average value: 73.9 MPa Grade Count:12 |
| Compressive Modulus | 2.70 - 3.00 GPa | 392 - 435 ksi | Average value: 2.84 GPa Grade Count:5 |
| Izod Impact, Notched | 0.267 - 6.41 J/cm | 0.500 - 12.0 ft-lb/in | Average value: 0.825 J/cm Grade Count:14 |
| 0.350 - 0.350 J/cm @Temperature -40.0 - -20.0 °C | 0.656 - 0.656 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.350 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 6.67 - 5340 J/cm | 12.5 - 10000 ft-lb/in | Average value: 9.98 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 2.50 - 100000 kJ/m2 | 1.19 - 47600 ft-lb/in2 | Average value: 6.56 kJ/m2 Grade Count:10 |
| 5.00 - 5.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 2.38 - 2.38 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 5.00 kJ/m2 Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:1 |
| Charpy Impact Unnotched | 5.00 J/cm2 - NB | 23.8 ft-lb/in2 - NB | Average value: 13.5 J/cm2 Grade Count:9 |
| 30.0 J/cm2 - NB @Temperature -40.0 - -20.0 °C | 143 ft-lb/in2 - NB @Temperature -40.0 - -4.00 °F | Average value: 30.0 J/cm2 Grade Count:2 | |
| Charpy Impact, Notched | 0.300 - 8.50 J/cm2 | 1.43 - 40.5 ft-lb/in2 | Average value: 1.41 J/cm2 Grade Count:9 |
| Coefficient of Friction | 0.0400 - 0.550 | 0.0400 - 0.550 | Average value: 0.209 Grade Count:14 |
| Tear Strength Test | 0.150 - 0.200 | 0.150 - 0.200 | Average value: 0.167 Grade Count:6 |
| K Factor (Wear Factor) | 1.00e-10 | 1.00e-10 | Average value: 1.00e-10 Grade Count:6 |
| K (wear) Factor | 91.0 - 181 x 10-8 mm3/N-M | 45.2 - 90.0 x 10-10 in3-min/ft-lb-hr | Average value: 134 x 10-8 mm3/N-M Grade Count:3 |
| Limiting Pressure Velocity | 0.0800 - 0.193 MPa-m/sec | 2280 - 5500 psi-ft/min | Average value: 0.127 MPa-m/sec Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+16 ohm-cm | 1.00e+12 - 1.00e+16 ohm-cm | Average value: 1.48e+15 ohm-cm Grade Count:15 |
| Surface Resistance | 1.00e+10 - 1.00e+13 ohm | 1.00e+10 - 1.00e+13 ohm | Average value: 3.58e+12 ohm Grade Count:14 |
| Dielectric Constant | 3.60 - 12.0 | 3.60 - 12.0 | Average value: 4.27 Grade Count:13 |
| Dielectric Strength | 15.0 - 50.0 kV/mm | 381 - 1270 kV/in | Average value: 28.9 kV/mm Grade Count:12 |
| Dissipation Factor | 0.00200 - 0.150 | 0.00200 - 0.150 | Average value: 0.0460 Grade Count:4 |
| Dielectric Loss Index | 0.0300 | 0.0300 | Average value: 0.0300 Grade Count:6 |
| Comparative Tracking Index | 550 - 604 V | 550 - 604 V | Average value: 594 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 - 100 μm/m-°C | 38.9 - 55.6 μin/in-°F | Average value: 81.3 μm/m-°C Grade Count:16 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | Average value: 1.67 J/g-°C Grade Count:8 |
| Thermal Conductivity | 0.250 - 0.300 W/m-K | 1.74 - 2.08 BTU-in/hr-ft2-°F | Average value: 0.262 W/m-K Grade Count:9 |
| Melting Point | 214 - 223 °C | 417 - 433 °F | Average value: 220 °C Grade Count:22 |
| Maximum Service Temperature, Air | 90.0 - 185 °C | 194 - 365 °F | Average value: 134 °C Grade Count:16 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 - 260 °C | 230 - 500 °F | Average value: 198 °C Grade Count:17 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 210 °C | 131 - 410 °F | Average value: 101 °C Grade Count:29 |
| Vicat Softening Point | 135 - 215 °C | 275 - 419 °F | Average value: 196 °C Grade Count:7 |
| Minimum Service Temperature, Air | -100 - -40.0 °C | -148 - -40.0 °F | Average value: -52.9 °C Grade Count:11 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:21 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 290 °C | 430 - 554 °F | Average value: 253 °C Grade Count:5 |
| Melt Temperature | 210 - 290 °C | 410 - 554 °F | Average value: 257 °C Grade Count:10 |
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | Average value: 78.3 °C Grade Count:13 |
| Drying Temperature | 75.0 - 100 °C | 167 - 212 °F | Average value: 84.9 °C Grade Count:10 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 2.33 hour Grade Count:6 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.150 % Grade Count:8 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:4 |
| Injection Pressure | 4.96 - 130 MPa | 720 - 18900 psi | Average value: 79.6 MPa Grade Count:11 |