- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 0.481
- 拉伸強度 [MPa]: 55.8
- 斷裂伸長率 [%]: 65.0
- 彎曲強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.70
- 硬度: 90.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.49 g/cc | 0.0405 - 0.0538 lb/in3 | Average value: 1.26 g/cc Grade Count:31 |
| Filler Content | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 17.8 % Grade Count:4 |
| Water Absorption | 0.600 - 5.70 % | 0.600 - 5.70 % | Average value: 1.44 % Grade Count:23 |
| Water Absorption at Saturation | 5.00 - 7.00 % | 5.00 - 7.00 % | Average value: 5.67 % Grade Count:3 |
| Viscosity Measurement | 145 | 145 | Average value: 145 Grade Count:3 |
| Linear Mold Shrinkage | 0.00400 - 0.0200 cm/cm | 0.00400 - 0.0200 in/in | Average value: 0.0125 cm/cm Grade Count:29 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0170 - 0.0180 cm/cm | 0.0170 - 0.0180 in/in | Average value: 0.0172 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90.0 - 120 | 90.0 - 120 | Average value: 112 Grade Count:16 |
| Ball Indentation Hardness | 110 - 115 MPa | 16000 - 16700 psi | Average value: 113 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 45.0 - 150 MPa | 6530 - 21800 psi | Average value: 70.5 MPa Grade Count:22 |
| Tensile Strength, Yield | 55.8 - 145 MPa | 8100 - 21000 psi | Average value: 83.2 MPa Grade Count:10 |
| Elongation at Break | 2.00 - 25.0 % | 2.00 - 25.0 % | Average value: 9.54 % Grade Count:27 |
| Elongation at Yield | 2.00 - 25.0 % | 2.00 - 25.0 % | Average value: 10.3 % Grade Count:5 |
| Modulus of Elasticity | 2.00 - 7.10 GPa | 290 - 1030 ksi | Average value: 2.96 GPa Grade Count:20 |
| Flexural Yield Strength | 65.0 - 268 MPa | 9430 - 38900 psi | Average value: 99.2 MPa Grade Count:30 |
| Flexural Modulus | 1.70 - 8.27 GPa | 247 - 1200 ksi | Average value: 2.96 GPa Grade Count:30 |
| Izod Impact, Notched | 0.481 - 0.801 J/cm | 0.900 - 1.50 ft-lb/in | Average value: 0.596 J/cm Grade Count:24 |
| Izod Impact, Unnotched | 5.34 - 16.0 J/cm | 10.0 - 30.0 ft-lb/in | Average value: 9.65 J/cm Grade Count:13 |
| Izod Impact, Notched (ISO) | 7.00 - 7.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 3.33 - 3.33 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 7.00 kJ/m2 Grade Count:1 |
| Izod Impact, Unnotched (ISO) | 75.0 - 75.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 35.7 - 35.7 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 75.0 kJ/m2 Grade Count:1 |
| Charpy Impact Unnotched | 8.00 J/cm2 - NB | 38.1 ft-lb/in2 - NB | Average value: 9.40 J/cm2 Grade Count:6 |
| 7.60 J/cm2 - NB @Temperature -40.0 - -30.0 °C | 36.2 ft-lb/in2 - NB @Temperature -40.0 - -22.0 °F | Average value: 7.60 J/cm2 Grade Count:4 | |
| Charpy Impact, Notched | 0.900 - 1.30 J/cm2 | 4.28 - 6.19 ft-lb/in2 | Average value: 1.01 J/cm2 Grade Count:6 |
| 0.700 - 0.700 J/cm2 @Temperature -30.0 - -30.0 °C | 3.33 - 3.33 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.700 J/cm2 Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+16 ohm-cm | 1.00e+13 - 1.00e+16 ohm-cm | Average value: 4.52e+14 ohm-cm Grade Count:17 |
| Dielectric Strength | 15.7 - 19.7 kV/mm | 400 - 500 kV/in | Average value: 17.7 kV/mm Grade Count:12 |
| Dissipation Factor | 0.0190 - 0.0200 | 0.0190 - 0.0200 | Average value: 0.0198 Grade Count:5 |
| Comparative Tracking Index | 500 V | 500 V | Average value: 500 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 27.0 - 93.6 μm/m-°C | 15.0 - 52.0 μin/in-°F | Average value: 70.3 μm/m-°C Grade Count:12 |
| Melting Point | 221 °C | 430 °F | Average value: 221 °C Grade Count:3 |
| Maximum Service Temperature, Air | 80.0 - 135 °C | 176 - 275 °F | Average value: 114 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 - 216 °C | 275 - 420 °F | Average value: 177 °C Grade Count:16 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 - 216 °C | 135 - 420 °F | Average value: 98.3 °C Grade Count:29 |
| Flammability, UL94 | HB | HB | Grade Count:19 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 221 - 271 °C | 430 - 520 °F | Average value: 252 °C Grade Count:9 |
| Melt Temperature | 243 - 300 °C | 470 - 572 °F | Average value: 269 °C Grade Count:10 |
| Mold Temperature | 54.4 - 110 °C | 130 - 230 °F | Average value: 76.3 °C Grade Count:16 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 85.0 °C Grade Count:11 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 2.44 hour Grade Count:8 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:8 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:7 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:13 |