- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 3.03
- 熱變形溫度 [℃]: 238.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ASTM D150 |
| Dielectric Strength | 22.6 kV/mm | 575 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 82.8 μm/m-°C @Temperature 20.0 °C | 46.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | 0.0590 in |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 140 rpm | 40 - 140 rpm | |