- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 1.15
- 缺口沖擊強(qiáng)度: 1.2
- 拉伸強(qiáng)度 [MPa]: 68.0
- 斷裂伸長(zhǎng)率 [%]: 85.0
- 彎曲模量 [MPa]: 2.50
- 熱變形溫度 [℃]: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ASTM D792 |
| Water Absorption | 1.15 % | 1.15 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Break | 28 % | 28 % | ASTM D638 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm @Thickness 3.17 mm | 2.25 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.20e+15 ohm-cm | 3.20e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.11 @Frequency 1e+6 Hz | 3.11 @Frequency 1e+6 Hz | ASTM D150 |
| 3.47 @Frequency 1000 Hz | 3.47 @Frequency 1000 Hz | ASTM D150 | |
| 3.56 @Frequency 100 Hz | 3.56 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | Step by step; ASTM D149 |
| 21.2 kV/mm | 538 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | ASTM D150 |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150 | |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 261 °C | 502 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C @Thickness 3.20 mm | 226 °F @Thickness 0.126 in | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 3.20 mm | 172 °F @Thickness 0.126 in | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |