- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.25
- 拉伸強度 [MPa]: 67.0
- 斷裂伸長率 [%]: 13.8
- 彎曲強度 [MPa]: 1.51
- 彎曲模量 [MPa]: 1.76
- 硬度: 105.0
- 熱變形溫度 [℃]: 124.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 - 1.61 g/cc | 0.0509 - 0.0582 lb/in3 | Average value: 1.49 g/cc Grade Count:92 |
| Filler Content | 36.0 - 40.0 % | 36.0 - 40.0 % | Average value: 39.7 % Grade Count:27 |
| Water Absorption | 0.0700 - 6.20 % | 0.0700 - 6.20 % | Average value: 2.04 % Grade Count:45 |
| Moisture Absorption at Equilibrium | 1.40 - 2.00 % | 1.40 - 2.00 % | Average value: 1.54 % Grade Count:19 |
| Water Absorption at Saturation | 5.00 - 7.00 % | 5.00 - 7.00 % | Average value: 5.26 % Grade Count:5 |
| Viscosity | 51000 - 490000 cP @Temperature 275 - 315 °C | 51000 - 490000 cP @Temperature 527 - 599 °F | Average value: 187000 cP Grade Count:1 |
| 51000 - 490000 cP @Shear Rate 500 - 7000 1/s | 51000 - 490000 cP @Shear Rate 500 - 7000 1/s | Average value: 187000 cP Grade Count:1 | |
| Viscosity Measurement | 0.520 - 145 | 0.520 - 145 | Average value: 37.0 Grade Count:4 |
| Linear Mold Shrinkage | 0.00200 - 0.0170 cm/cm | 0.00200 - 0.0170 in/in | Average value: 0.00947 cm/cm Grade Count:77 |
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.0200 cm/cm | 0.00600 - 0.0200 in/in | Average value: 0.0110 cm/cm Grade Count:36 |
| Melt Flow | 1.00 - 5.00 g/10 min | 1.00 - 5.00 g/10 min | Average value: 3.00 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60.0 - 97.0 | 60.0 - 97.0 | Average value: 88.6 Grade Count:10 |
| Hardness, Rockwell R | 105 - 122 | 105 - 122 | Average value: 120 Grade Count:22 |
| Tensile Strength, Ultimate | 1.51 - 193 MPa | 219 - 28000 psi | Average value: 56.7 MPa Grade Count:62 |
| 32.0 - 128 MPa @Temperature -40.0 - 121 °C | 4640 - 18600 psi @Temperature -40.0 - 250 °F | Average value: 36.2 MPa Grade Count:5 | |
| 0.580 - 128.4 MPa @Temperature -40.0 - 150 °C | 84.1 - 18620 psi @Temperature -40.0 - 302 °F | Average value: 36.2 MPa Grade Count:4 | |
| 0.580 - 128.4 MPa @Strain 0.100 - 52.0 % | 84.1 - 18620 psi @Strain 0.100 - 52.0 % | Average value: 36.2 MPa Grade Count:4 | |
| Tensile Strength, Yield | 67.0 - 128 MPa | 9720 - 18500 psi | Average value: 90.6 MPa Grade Count:28 |
| Elongation at Break | 1.00 - 45.0 % | 1.00 - 45.0 % | Average value: 8.65 % Grade Count:74 |
| 3.00 - 79.0 % @Temperature -40.0 - 121 °C | 3.00 - 79.0 % @Temperature -40.0 - 250 °F | Average value: 45.4 % Grade Count:2 | |
| Elongation at Yield | 1.50 - 35.0 % | 1.50 - 35.0 % | Average value: 7.33 % Grade Count:15 |
| Modulus of Elasticity | 1.60 - 10.0 GPa | 232 - 1450 ksi | Average value: 6.18 GPa Grade Count:42 |
| Flexural Yield Strength | 13.8 - 193 MPa | 2000 - 28000 psi | Average value: 129 MPa Grade Count:57 |
| Flexural Modulus | 1.76 - 10.3 GPa | 255 - 1500 ksi | Average value: 6.14 GPa Grade Count:78 |
| 0.620 - 6.55 GPa @Temperature -40.0 - 121 °C | 89.9 - 950 ksi @Temperature -40.0 - 250 °F | Average value: 2.37 GPa Grade Count:6 | |
| Shear Modulus | 1.91 - 2.56 GPa | 277 - 371 ksi | Average value: 2.34 GPa Grade Count:3 |
| 0.0420 - 2.27 GPa @Temperature -50.0 - 250 °C | 6.09 - 329 ksi @Temperature -58.0 - 482 °F | Average value: 0.825 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.250 - 1.88 J/cm | 0.468 - 3.52 ft-lb/in | Average value: 0.555 J/cm Grade Count:53 |
| 0.250 - 0.800 J/cm @Temperature -40.0 - -20.0 °C | 0.468 - 1.50 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.483 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 1.60 - 16.0 J/cm | 3.00 - 30.0 ft-lb/in | Average value: 5.51 J/cm Grade Count:14 |
| Izod Impact, Notched (ISO) | 3.10 - 13.0 kJ/m2 | 1.48 - 6.19 ft-lb/in2 | Average value: 5.87 kJ/m2 Grade Count:27 |
| 2.50 - 6.00 kJ/m2 @Temperature -40.0 - -30.0 °C | 1.19 - 2.86 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 4.94 kJ/m2 Grade Count:7 | |
| Izod Impact, Unnotched (ISO) | 95.0 - 330 kJ/m2 | 45.2 - 157 ft-lb/in2 | Average value: 195 kJ/m2 Grade Count:4 |
| 50.0 - 100 kJ/m2 @Temperature -30.0 - -30.0 °C | 23.8 - 47.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 83.3 kJ/m2 Grade Count:3 | |
| Charpy Impact Unnotched | 1.50 - 1000 J/cm2 | 7.14 - 4760 ft-lb/in2 | Average value: 8.37 J/cm2 Grade Count:34 |
| 1.10 - 12.0 J/cm2 @Temperature -40.0 - 30.0 °C | 5.24 - 57.1 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 4.67 J/cm2 Grade Count:25 | |
| Charpy Impact, Notched | 0.200 - 1.50 J/cm2 | 0.952 - 7.14 ft-lb/in2 | Average value: 0.627 J/cm2 Grade Count:30 |
| 0.150 - 0.620 J/cm2 @Temperature -40.0 - 30.0 °C | 0.714 - 2.95 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 0.345 J/cm2 Grade Count:23 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 8500 MPa | 0.000 - 1.23e+6 psi | Average value: 1280 MPa Grade Count:3 |
| 0.000 - 20.0 MPa @Temperature 60.0 - 100 °C | 0.000 - 2900 psi @Temperature 140 - 212 °F | Average value: 7.27 MPa Grade Count:1 | |
| 0.000 - 20.0 MPa @Strain 0.000 - 1.94 % | 0.000 - 2900 psi @Strain 0.000 - 1.94 % | Average value: 7.27 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 20.0 MPa @Temperature 60.0 - 100 °C | 0.000 - 2900 psi @Temperature 140 - 212 °F | Average value: 7.27 MPa Grade Count:1 |
| 0.000 - 20.0 MPa @Strain 0.000 - 2.96 % | 0.000 - 2900 psi @Strain 0.000 - 2.96 % | Average value: 7.27 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.00e+17 ohm-cm | 1.00e+8 - 1.00e+17 ohm-cm | Average value: 8.12e+15 ohm-cm Grade Count:35 |
| Surface Resistance | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | Average value: 2.09e+13 ohm Grade Count:14 |
| Dielectric Constant | 3.20 - 12.6 | 3.20 - 12.6 | Average value: 4.93 Grade Count:14 |
| Dielectric Strength | 15.0 - 158 kV/mm | 380 - 4010 kV/in | Average value: 31.9 kV/mm Grade Count:33 |
| Dissipation Factor | 0.00800 - 0.440 | 0.00800 - 0.440 | Average value: 0.0736 Grade Count:10 |
| Comparative Tracking Index | 300 - 600 V | 300 - 600 V | Average value: 522 V Grade Count:26 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 - 500 μm/m-°C | 3.33 - 278 μin/in-°F | Average value: 268 μm/m-°C Grade Count:28 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:5 | |
| CTE, linear, Transverse to Flow | 6.30 - 86.0 μm/m-°C | 3.50 - 47.8 μin/in-°F | Average value: 55.4 μm/m-°C Grade Count:11 |
| 98.0 - 110 μm/m-°C @Temperature 55.0 - 160 °C | 54.4 - 61.1 μin/in-°F @Temperature 131 - 320 °F | Average value: 100 μm/m-°C Grade Count:5 | |
| Melting Point | 254 - 325 °C | 489 - 617 °F | Average value: 260 °C Grade Count:58 |
| Maximum Service Temperature, Air | 80.0 - 250 °C | 176 - 482 °F | Average value: 142 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 - 260 °C | 255 - 500 °F | Average value: 230 °C Grade Count:45 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 - 254 °C | 167 - 490 °F | Average value: 168 °C Grade Count:83 |
| Vicat Softening Point | 230 - 265 °C | 446 - 509 °F | Average value: 245 °C Grade Count:15 |
| UL RTI, Electrical | 65.0 - 120 °C | 149 - 248 °F | Average value: 78.5 °C Grade Count:9 |
| UL RTI, Mechanical with Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 73.3 °C Grade Count:9 |
| UL RTI, Mechanical without Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 76.3 °C Grade Count:9 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:45 |
| Oxygen Index | 22.0 - 30.0 % | 22.0 - 30.0 % | Average value: 25.7 % Grade Count:7 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 722 °C Grade Count:9 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 310 °C | 518 - 590 °F | Average value: 288 °C Grade Count:7 |
| Nozzle Temperature | 263 - 295 °C | 505 - 563 °F | Average value: 282 °C Grade Count:8 |
| Melt Temperature | 208 - 310 °C | 406 - 590 °F | Average value: 282 °C Grade Count:42 |
| Mold Temperature | 26.7 - 120 °C | 80.0 - 248 °F | Average value: 88.8 °C Grade Count:46 |
| Drying Temperature | 60.0 - 100 °C | 140 - 212 °F | Average value: 80.4 °C Grade Count:36 |
| Dry Time | 1.00 - 5.00 hour | 1.00 - 5.00 hour | Average value: 3.27 hour Grade Count:32 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.183 % Grade Count:21 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Injection Pressure | 34.5 - 140 MPa | 5000 - 20300 psi | Average value: 90.7 MPa Grade Count:23 |
| Hold Pressure | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 91.9 MPa Grade Count:4 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 4.03 MPa Grade Count:12 |
| Clamp Pressure | 26.7 - 68.7 MPa | 3870 - 9960 psi | Average value: 47.5 MPa Grade Count:3 |
| Cushion | 0.300 - 6.40 cm | 0.118 - 2.52 in | Average value: 1.88 cm Grade Count:3 |
| Screw Speed | 30.0 - 120 rpm | 30.0 - 120 rpm | Average value: 68.5 rpm Grade Count:13 |