- 密度 [g/cm3]: 1.75
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.75 - 1.78 g/cc | 0.0632 - 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.20 % @Temperature 23.0 °C, Time 86400 sec | <= 0.20 % @Temperature 73.4 °F, Time 24.0 hour | 30g; ASTM D543 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Modulus | 1.00 - 1.50 GPa @Temperature 23.0 °C | 145 - 218 ksi @Temperature 73.4 °F | 1.0 mm/min; ASTM D638 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA, after 2 min @ 23°C; ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1V, after 2 min - 500 V @ 23°C; ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 40.0 - 48.0 J/g | 17.2 - 20.6 BTU/lb | 80°C to end of melting; ASTM D3418 | ||
| Melting Point | 158 - 166 °C | 316 - 331 °F | ASTM D3418 | ||
| Crystallization Temperature | 135 - 140 °C | 275 - 284 °F | Peak, DSC; ASTM D3418 | ||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | DSC | ||
| Decomposition Temperature | >= 375 °C | >= 707 °F | @ 1% weight loss; TGA | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Very high Viscosity | ||||
| Generic | PVDF | ||||
| Uses | Batteries | ||||
| Binder | |||||