- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.75
- 拉伸強度 [MPa]: 14.0
- 斷裂伸長率 [%]: 8.00
- 彎曲強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 0.200
- 熱變形溫度 [℃]: 48.0
- 脆化溫度 [℃]: -53.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in3 | ISO 1183 |
| Water Absorption | <= 0.040 % | <= 0.040 % | ISO 62 (method 1) |
| Linear Mold Shrinkage | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 15 g/10 min @Load 5.00 kg, Temperature 230 °C | 15 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 47 @Thickness 2.00 mm | 47 @Thickness 0.0787 in | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 14.0 - 35.0 MPa | 2030 - 5080 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 350 - 600 % | 350 - 600 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 10 - 12 % | 10 - 12 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 0.200 GPa | 29.0 ksi | 1 mm/min; ASTM D638 |
| Flexural Yield Strength | 8.00 MPa | 1160 psi | 2 mm/min; ASTM D790 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | 2 mm/min; ASTM D790 |
| Izod Impact, Notched | NB @Thickness 4.00 mm, Temperature 23.0 °C | NB @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 15 | 5.0 - 15 | CS10 / 1 kg |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 17.0 J/g | 7.31 BTU/lb | 80°C to end of melting |
| 19.0 J/g | 8.17 BTU/lb | Crystallization Heat | |
| CTE, linear | 130 - 150 μm/m-°C @Temperature 20.0 °C | 72.2 - 83.3 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 168 °C | 334 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 128 °C | 262 °F | |
| Maximum Service Temperature, Air | 320 - 340 °C | 608 - 644 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C @Thickness 4.00 mm | 118 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Vicat Softening Point | 75.0 °C @Load 1.00 kg, Thickness 4.00 mm | 167 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| Brittleness Temperature | -53.0 °C | -63.4 °F | ASTM D746A |
| Glass Transition Temp, Tg | -28.0 °C | -18.4 °F | DMTA |
| Oxygen Index | 50 - 65 % @Thickness 3.00 mm | 50 - 65 % @Thickness 0.118 in | sheet; ASTM D2863 |