- 熔體流動速率 [g/10min]: 2.5
- 缺口沖擊強度: 10.0
- 拉伸強度 [MPa]: 34.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |||
| Melt Flow | 2.5 - 4.0 g/10 min @Load 10.0 kg, Temperature 230 °C | 2.5 - 4.0 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 @Thickness 2.00 mm | 70 @Thickness 0.0787 in | ASTM D2240 | ||
| Tensile Strength at Break | 34.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 4930 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 34.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 4930 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 100 - 300 % @Thickness 2.00 mm, Temperature 23.0 °C | 100 - 300 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 9.0 - 12 % @Thickness 2.00 mm, Temperature 23.0 °C | 9.0 - 12 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 1.25 - 1.40 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 181 - 203 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
| Izod Impact, Notched | 10.0 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 18.7 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | 2 m/s, Partial Break; ASTM D6110 | ||
| Coefficient of Friction, Dynamic | 0.20 - 0.30 | 0.20 - 0.30 | vs. Itself; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 | ||
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 @Load 1.00 kg | 5.0 - 10 @Load 2.20 lb | CS-10 Wheel; ASTM D4060 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 41.0 - 50.0 J/g | 17.6 - 21.5 BTU/lb | ASTM D3417 | ||
| 42.0 - 50.0 J/g | 18.1 - 21.5 BTU/lb | Crystallization Heat; ASTM D3417 | |||
| CTE, linear, Parallel to Flow | 130 - 180 μm/m-°C @Temperature 0.000 - 40.0 °C | 72.2 - 100 μin/in-°F @Temperature 32.0 - 104 °F | ASTM D696 | ||
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C | 0.287 BTU/lb-°F @Temperature 73.4 °F | ASTM E968 | ||
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM E968 | |||
| Thermal Conductivity | 0.200 W/m-K @Temperature 23.0 °C | 1.39 BTU-in/hr-ft2-°F @Temperature 73.4 °F | ASTM C177 | ||
| Melting Point | 170 - 174 °C | 338 - 345 °F | ASTM D3418 | ||
| Crystallization Temperature | 142 - 146 °C | 288 - 295 °F | Peak, DSC; ASTM D3418 | ||
| Vicat Softening Point | 167 °C | 333 °F | Rate A (50°C/h), Loading 2 (50 N); ASTM D1525 | ||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Copolymer | ||||
| High Viscosity | |||||
| Generic | PVDF | ||||
| Uses | Piping | ||||