- 熔體流動速率 [g/10min]: 0.2
- 拉伸強度 [MPa]: 53.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Melt Flow | <= 0.20 g/10 min @Load 21.6 kg, Temperature 230 °C | <= 0.20 g/10 min @Load 47.6 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 25.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 3630 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 7690 - 8270 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 15 - 50 % @Thickness 2.00 mm, Temperature 23.0 °C | 15 - 50 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C | 5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 1.60 - 1.70 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 232 - 247 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 47.0 - 52.0 J/g | 20.2 - 22.4 BTU/lb | Crystallization Heat; ASTM D3417 | ||
| 57.0 - 66.0 J/g | 24.5 - 28.4 BTU/lb | ASTM D3417 | |||
| Melting Point | 171 - 175 °C | 340 - 347 °F | ASTM D3418 | ||
| Crystallization Temperature | 133 - 138 °C | 271 - 280 °F | Peak, DSC; ASTM D3418 | ||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Homopolymer | ||||
| Very high Viscosity | |||||
| Forms | Powder | ||||
| Generic | PVDF | ||||
| Uses | Batteries | ||||
| Membranes | |||||