- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.78
- 拉伸強度 [MPa]: 48.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | Method 1; ISO 62 | ||
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 18 - 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 18 - 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 30.0 MPa @Temperature 23.0 °C | 4350 psi @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 48.0 MPa @Temperature 23.0 °C | 6960 psi @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 7.0 % @Temperature 23.0 °C | 7.0 % @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 1.90 GPa @Temperature 23.0 °C | 276 ksi @Temperature 73.4 °F | 1.0 mm/min; ASTM D638 | ||
| Charpy Impact, Notched | 0.850 J/cm2 | 4.04 ft-lb/in2 | 4 mm thick, 2 m/s; ASTM D256 | ||
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | vs. Itself; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.32 | 0.32 | vs. Itself; ASTM D1894 | ||
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | CS-10 Wheel; ISO 5470-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 51.6 J/g | 22.2 BTU/lb | Crystallization Heat; ASTM D3418 | ||
| 52.7 J/g | 22.7 BTU/lb | 80°C to end of melting; ASTM D3418 | |||
| Melting Point | 169 °C | 336 °F | ASTM D3418 | ||
| Crystallization Temperature | 136 °C | 277 °F | Peak, DSC; ASTM D3418 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Generic | PVDF | ||||
| Processing Method | Coextrusion | ||||