- 熔體流動速率 [g/10min]: 7.0
- 拉伸強度 [MPa]: 45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |||
| Melt Flow | 7.0 - 13 g/10 min @Load 3.80 kg, Temperature 230 °C | 7.0 - 13 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 | ||
| 10 - 20 g/10 min @Load 5.00 kg, Temperature 230 °C | 10 - 20 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 73 - 80 @Thickness 2.00 mm, Time 1.00 sec | 73 - 80 @Thickness 0.0787 in, Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 45.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 6530 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 20 - 300 % @Thickness 2.00 mm, Temperature 23.0 °C | 20 - 300 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C | 5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 1.40 - 2.20 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 203 - 319 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
| Impact | 37.4 - 107 @Thickness 4.00 mm | 37.4 - 107 @Thickness 0.157 in | J/m Charpy Notched Impact Strength; 2 m/s; ASTM D6110 | ||
| Coefficient of Friction, Dynamic | 0.15 - 0.35 | 0.15 - 0.35 | vs. Itself; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 | ||
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 @Load 1.00 kg | 5.0 - 10 @Load 2.20 lb | CS-10 Wheel; ASTM D4060 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Dielectric Strength | 0.787 - 0.984 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 20.0 - 25.0 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 53.0 - 60.0 J/g | 22.8 - 25.8 BTU/lb | Crystallization Heat; ASTM D3418 | ||
| 53.0 - 60.0 J/g | 22.8 - 25.8 BTU/lb | ASTM D3418 | |||
| CTE, linear, Parallel to Flow | 140 μm/m-°C | 77.8 μin/in-°F | ASTM D696 | ||
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C | 0.287 BTU/lb-°F @Temperature 73.4 °F | ASTM C351 | ||
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM C351 | |||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ASTM C177 | ||
| Melting Point | 162 - 168 °C | 324 - 334 °F | ASTM D3418 | ||
| Crystallization Temperature | 133 - 140 °C | 271 - 284 °F | Peak, DSC; ASTM D3418 | ||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
| Flammability, UL94 | V-0 @Thickness 0.100 mm | V-0 @Thickness 0.00394 in | UL 94 | ||
| Oxygen Index | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | ASTM D2863 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Homopolymer | ||||
| Medium Viscosity | |||||
| Generic | PVDF | ||||
| Processing Method | Film Extrusion | ||||
| Injection Molding | |||||