- 熔體流動速率 [g/10min]: 3.0
- 拉伸強度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Melt Flow | 3.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 3.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 2900 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 15.0 - 18.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 2180 - 2610 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 600 - 750 % @Thickness 2.00 mm, Temperature 23.0 °C | 600 - 750 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 12 - 15 % @Thickness 2.00 mm, Temperature 23.0 °C | 12 - 15 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 0.360 - 0.480 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 52.2 - 69.6 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 20.0 - 24.0 J/g | 8.60 - 10.3 BTU/lb | Crystallization Heat; ASTM D3417 | ||
| 20.0 - 24.0 J/g | 8.60 - 10.3 BTU/lb | ASTM D3417 | |||
| Melting Point | 130 - 136 °C | 266 - 277 °F | ASTM D3418 | ||
| Crystallization Temperature | 89.0 - 93.0 °C | 192 - 199 °F | Peak, DSC; ASTM D3418 | ||
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Copolymer | ||||
| Low Viscosity | |||||
| Generic | PVDF | ||||
| Processing Method | Solution Processing | ||||
| Uses | Batteries | ||||