- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.78
- 缺口沖擊強度: 0.55
- 拉伸強度 [MPa]: 53.0
- 斷裂伸長率 [%]: 78.0
- 彎曲強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 2.20
- 熱變形溫度 [℃]: 148.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 |
| Water Absorption | <= 0.040 % | <= 0.040 % | ISO 62 (method 1) |
| Linear Mold Shrinkage | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 78 @Thickness 2.00 mm | 78 @Thickness 0.0787 in | ASTM D2240 |
| Tensile Strength, Ultimate | 35.0 - 50.0 MPa | 5080 - 7250 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 - 57.0 MPa | 7690 - 8270 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 20 - 50 % | 20 - 50 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 - 10 % | 5.0 - 10 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 2.60 GPa | 377 ksi | 1 mm/min; ASTM D638 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 2 mm/min; ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 1.03 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 | 5.0 - 10 | CS10 / 1 kg |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 59.0 J/g | 25.4 BTU/lb | Crystallization Heat |
| 67.0 J/g | 28.8 BTU/lb | 80°C to end of melting | |
| CTE, linear | 120 - 140 μm/m-°C @Temperature 20.0 °C | 66.7 - 77.8 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 174 °C | 345 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 140 °C | 284 °F | |
| Maximum Service Temperature, Air | 375 - 400 °C | 707 - 752 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C @Thickness 4.00 mm | 298 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 4.00 mm | 239 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Vicat Softening Point | 171 °C @Load 1.00 kg, Thickness 4.00 mm | 340 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| Brittleness Temperature | 0.000 - 10.0 °C | 32.0 - 50.0 °F | ASTM D746A |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F | DMTA |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | sheet; ASTM D2863 |