- 熔體流動速率 [g/10min]: 10.0
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 11.0
- 拉伸強度 [MPa]: 48.0
- 斷裂伸長率 [%]: 55.0
- 彎曲模量 [MPa]: 1.52
- 熱變形溫度 [℃]: 127.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | ASTM D792 | ||
| Water Absorption | 0.020 % @Temperature 23.0 °C, Time 86400 sec | 0.020 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Viscosity | 2.60e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 2.60e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt; ASTM D3835 | ||
| Melt Flow | 10 g/10 min @Load 21.6 kg, Temperature 230 °C | 10 g/10 min @Load 47.6 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 | 75 | ASTM D2240 | ||
| Tensile Strength at Break | 41.0 MPa @Temperature 23.0 °C | 5950 psi @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 48.0 MPa @Temperature 23.0 °C | 6960 psi @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 100 % @Temperature 23.0 °C | 100 % @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 1.31 GPa @Temperature 23.0 °C | 190 ksi @Temperature 73.4 °F | 50 mm/min; ASTM D638 | ||
| Flexural Yield Strength | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50 mm/min; ASTM D790 | ||
| Flexural Modulus | 1.52 GPa @Temperature 23.0 °C | 220 ksi @Temperature 73.4 °F | 50 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D256 | ||
| 1.10 J/cm @Temperature 23.0 °C | 2.06 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | vs. Itself; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.30 | 0.30 | vs. Itself; ASTM D1894 | ||
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | CS-17 Wheel | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | 50% RH; ASTM D257 | ||
| Dielectric Constant | 6.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 6.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | ||
| Dielectric Strength | 0.394 kV/mm @Thickness 3.18 mm, Temperature 23.0 °C | 10.0 kV/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 46.0 J/g | 19.8 BTU/lb | Crystallization Heat; ASTM D3418 | ||
| 46.0 J/g | 19.8 BTU/lb | ASTM D3418 | |||
| CTE, linear, Parallel to Flow | 130 μm/m-°C | 72.2 μin/in-°F | ASTM D696 | ||
| Specific Heat Capacity | 1.34 J/g-°C | 0.320 BTU/lb-°F | ASTM D3418 | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ASTM D433 | ||
| Melting Point | 160 °C | 320 °F | ASTM D3418 | ||
| Crystallization Temperature | 132 °C | 270 °F | Peak, DSC; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Annealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Annealed; ASTM D648 | ||
| Glass Transition Temp, Tg | -39.0 °C | -38.2 °F | ASTM D4065 | ||
| Flammability, UL94 | V-0 | V-0 | UL 94 | ||
| Oxygen Index | 44 % | 44 % | ASTM D2863 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.42 | 1.42 | ASTM D542 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | High Viscosity | ||||
| Homopolymer | |||||
| Generic | PVDF | ||||
| Processing Method | Extrusion | ||||