- 熔體流動速率 [g/10min]: 4.2
- 密度 [g/cm3]: 0.938
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D 792 | ||
| Thickness | 20.0 microns | 0.787 mil | |||
| Melt Flow | 4.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 19 g | 19 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 320 g | 320 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 0.950 g/micron | 24.1 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 16.0 g/micron | 406 g/mil | ASTM D 1922 | ||
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 340 MPa | 49300 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 430 MPa | 62400 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D 1003 | ||
| Gloss | 88 % | 88 % | 45°; ASTM D 2457 | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 3 (ft-lb/mil) | NOVA Chemicals test method | |||