- 熔體流動速率 [g/10min]: 0.96
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D792 | ||
| Thickness | 25.0 - 75.0 microns | 0.984 - 2.95 mil | |||
| Melt Flow | 0.96 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.96 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | ASTM D2240 | ||
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 | ||
| Coefficient of Friction | 0.50 | 0.50 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 6.00 g/micron | 152 g/mil | ASTM D1922 | ||
| Dart Drop | 2.00 g/micron | 50.8 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | 1 mil; ASTM D1003 | ||
| Gloss | 58 % | 58 % | at 45°; 1 mil; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |||
| Die Opening | 0.0900 - 0.220 cm | 0.0354 - 0.0866 in | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.