- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.936
- 拉伸強度 [MPa]: 17.2
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | ASTM D638 |
| Elongation at Break | 1100 % | 1100 % | ASTM D638 |
| Puncture Energy | 0.275 J | 0.203 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 19 g | 19 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D1922 |
| Dart drop Test | 40.0 g | 0.0882 lb | ASTM D1709/A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | NOVA |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |