- 熔體流動速率 [g/10min]: 5.2
- 密度 [g/cm3]: 0.939
- 拉伸強度 [MPa]: 20.0
- 彎曲強度 [MPa]: 27.1
- 彎曲模量 [MPa]: 0.740
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | Compression Molded; ASTM D792 |
| ESCR 10% Igepal? | >= 50 hour | >= 50 hour | Compression Molded; ARM Method |
| Melt Flow | 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.2 g/10 min @Load 4.76 lb, Temperature 374 °F | Compression Molded; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | Compression Molded; ASTM D2240 |
| Tensile Strength, Ultimate | 27.1 MPa | 3930 psi | Compression Molded; ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | Compression Molded; ASTM D638 |
| Elongation at Break | 920 % | 920 % | Ultimate; Compression Molded; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | Compression Molded; ASTM D638 |
| Flexural Modulus | 0.740 GPa | 107 ksi | Compression Molded; ASTM D790 |
| Impact Test | 27.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 19.9 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Rotational Molded, Instrumented |
| 54.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 39.8 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Rotational Molded; ARM Method | |
| 108 J @Thickness 3.17 mm, Temperature -40.0 °C | 79.7 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Rotational Molded, Instrumented | |
| 230 J @Thickness 3.17 mm, Temperature -40.0 °C | 170 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Rotational Molded; ARM Method | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Compression Molded; ASTM E794 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | Compression Molded; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | Compression Molded; ASTM D648 |
| Vicat Softening Point | 121 °C | 250 °F | Compression Molded; ASTM D1525 |