- 熔體流動速率 [g/10min]: 2.6
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D 792 | ||
| Thickness | 25.0 microns | 0.984 mil | As tested for properties on this data sheet | ||
| Melt Flow | 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 14.2 MPa | 2060 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 15.1 MPa | 2190 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 40 g | 40 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 1.60 g/micron | 40.6 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 14.0 g/micron | 356 g/mil | ASTM D 1922 | ||
| Dart Drop | 1.60 g/micron | 40.6 g/mil | ASTM D 1709/A | ||
| Dart drop Test | 40.0 g | 0.0882 lb | F50; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 300 MPa | 43500 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 370 MPa | 53700 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.8 % | 4.8 % | ASTM D 1003 | ||
| Gloss | 80 % | 80 % | At 45°; ASTM D 2457 | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 24 (J/mm) | NOVA Chemicals test method | |||