- 熔體流動速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.941
- 拉伸強(qiáng)度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | 30 hour | 30 hour | F50; Condition A, 100% Igepal; ASTM D1693 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 190 °C | 11 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 400 % | 400 % | 50 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |