- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.955
- 拉伸強度 [MPa]: 29.0
- 彎曲強度 [MPa]: 36.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM D792 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 36.0 MPa | 5220 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 2000 % | 2000 % | ASTM D638 |