- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.962
- 缺口沖擊強度: 0.49
- 拉伸強度 [MPa]: 32.4
- 彎曲強度 [MPa]: 16.7
- 彎曲模量 [MPa]: 1.08
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 4.0 hour | 4.0 hour | ASTM D1693 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.7 MPa | 2420 psi | ASTM D638 |
| Tensile Strength, Yield | 32.4 MPa | 4690 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.08 GPa | 156 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 134 °C | 273 °F | ASTM D2117 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |