- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.958
- 缺口沖擊強度: 0.196
- 拉伸強度 [MPa]: 28.4
- 彎曲強度 [MPa]: 19.6
- 彎曲模量 [MPa]: 0.981
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 2.0 hour | 2.0 hour | ASTM D1693 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.6 MPa | 2840 psi | ASTM D638 |
| Tensile Strength, Yield | 28.4 MPa | 4120 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.981 GPa | 142 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 0.196 J/cm | 0.367 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | ASTM D2117 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |