- 密度 [g/cm3]: 0.941
- 拉伸強度 [MPa]: 23.4
- 硬度: 64.0
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ASTM D792 |
| Molecular Weight | >= 4.20e+6 g/mol | >= 4.20e+6 g/mol | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 64 | 64 | ASTM D785 |
| Hardness, Shore D | 67 | 67 | 15 seconds; ASTM D2240 |
| Tensile Strength at Break | 44.1 MPa | 6400 psi | 2"/min; ASTM D638 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | 2"/min; ASTM D638 |
| Elongation at Break | 350 % | 350 % | 2"/min; ASTM D638 |
| Elongation at Yield | 14 % | 14 % | ASTM D638 |
| 1% Secant Modulus | 1210 MPa | 175000 psi | ASTM D790B |
| Izod Impact, Unnotched | NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256A |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256A | |
| Coefficient of Friction | 0.11 | 0.11 | Gar-Dur to Gar-Dur |
| 0.13 | 0.13 | To stainless steel | |
| 0.14 | 0.14 | To rolled steel | |
| Abrasion | 10 | 10 | Relative, where Carbon Steel is 100 and Nylon 6/6 is 24 in; Sand Slurry Test |
| Compression Set | 0.60 % | 0.60 % | 24 hours after removal of 282 psi compressive stress at 20°C |
| 0.90 % | 0.90 % | 1 minute after removal of 282 psi compressive stress at 20°C | |
| 3.5 % | 3.5 % | 24 hours after removal of 1700 psi compressive stress at 20°C | |
| 5.4 % | 5.4 % | 1 minute after removal of 1700 psi compressive stress at 20°C | |
| 1.1 % @Temperature 80.0 °C | 1.1 % @Temperature 176 °F | 24 hours after removal of 282 psi compressive stress | |
| 1.6 % @Temperature 80.0 °C | 1.6 % @Temperature 176 °F | 1 minute after removal of 282 psi compressive stress | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 164 μm/m-°C @Temperature 20.0 °C | 91.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 130 - 131 °C | 266 - 268 °F | Crystalline MP |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ASTM D648 |
| Vicat Softening Point | 136 °C | 277 °F | ASTM D1525B |