- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 29.0
- 熱變形溫度 [℃]: 69.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 66 | 66 | DIN 53505 | ||
| Ball Indentation Hardness | 55.0 MPa | 7980 psi | ISO 2039 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 | ||
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ISO 527 | ||
| Elongation at Break | 55 % | 55 % | ISO 527 | ||
| Elongation at Yield | 13 % | 13 % | ISO 527 | ||
| Modulus of Elasticity | 1.36 GPa | 197 ksi | ISO 527 | ||
| Flexural Strength | 24.0 MPa | 3480 psi | 3.5%; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | >= 0.500 J/cm2 | >= 2.38 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1.00e+6 ohm-cm | <= 1.00e+6 ohm-cm | IEC 60093 | ||
| Surface Resistivity per Square | <= 100000 ohm | <= 100000 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 150 μm/m-°C @Temperature 20.0 °C | 83.3 μin/in-°F @Temperature 68.0 °F | DIN 53752 | ||
| Melting Point | 190 °C | 374 °F | DIN EN ISO 314 | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 | ||
| Vicat Softening Point | 83.0 °C | 181 °F | VST/B/50; ISO 306 | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Bondability | yes | ||||
| Color | Black | ||||
| UV Stabilization | limited | ||||