- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.03
- 脆化溫度 [℃]: -84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 30 hour | 30 hour | Condition B, F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Elongation at Yield | >= 600 % | >= 600 % | Ultimate, 2" (50mm) per min, Type IV; ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -84.0 °C | <= -119 °F | ASTM D746 |