- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.31
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | Condition B, F50; ASTM D1693 |
| ESCR 100% Igepal? | 50 hour | 50 hour | Condition A, F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Elongation at Yield | >= 600 % | >= 600 % | Ultimate, 2" (50mm) per min, Type IV; ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |