- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 29.0
- 彎曲模量 [MPa]: 1.34
- 熱變形溫度 [℃]: 74.0
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | Condition B, F50; ASTM D1693 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.5 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition F; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 29.0 MPa | 4200 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Elongation at Yield | >= 600 % | >= 600 % | Ultimate, 2" (50mm) per min, Type IV; ASTM D638 |
| Flexural Modulus | 1.34 GPa | 195 ksi | ASTM D790 |
| Tensile Impact Strength | 451 kJ/m2 | 215 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | no specified load; ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |