- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.939
- 拉伸強度 [MPa]: 19.3
- 彎曲模量 [MPa]: 0.621
- 脆化溫度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 5000 hour | >= 5000 hour | Condition A,B,C (100% Igepal), F50; ASTM D1693 |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg, Temperature 190 °C | 20 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 1000 hour | >= 1000 hour | ASTM F1473 |
| Tensile Strength at Break | 33.1 MPa | 4800 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Elongation at Break | >= 500 % | >= 500 % | 2" (50mm) per min.; ASTM D630 Type IV |
| Flexural Modulus | 0.621 GPa | 90.0 ksi | ASTM D3350 |
| 0.758 GPa | 110 ksi | ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D746 |