- 熔體流動速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.964
- 拉伸強度 [MPa]: 30.3
- 彎曲模量 [MPa]: 1.65
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.964 g/cc | 0.0348 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 10 hour | 10 hour | Condition B, F50; ASTM D1693 |
| 15 - 20 hour | 15 - 20 hour | Condition A (100% Igepal), F50; ASTM D1693 | |
| Melt Flow | 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.65 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.3 MPa | 4400 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Elongation at Break | >= 300 % | >= 300 % | 2" (50mm) per min.; ASTM D638 Type IV |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |