- 密度 [g/cm3]: 0.937
- 拉伸強度 [MPa]: 17.9
- 彎曲模量 [MPa]: 0.827
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1500 hour | >= 1500 hour | Condition C (100% Igepal), F50; ASTM D1693 |
| >= 1500 hour | >= 1500 hour | Condition B (10% Igepal), F50; ASTM D1693 | |
| High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C | 12 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Elongation at Break | >= 700 % | >= 700 % | 2" (50mm) per min.; ASTM D638 |
| Flexural Modulus | 0.827 GPa | 120 ksi | ASTM D790 |