- 熔體流動速率 [g/10min]: 0.08
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 17.9
- 彎曲模量 [MPa]: 0.827
- 熱變形溫度 [℃]: 59.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | SP-NCTL; ASTM D5397 |
| ESCR 100% Igepal? | >= 1500 hour | >= 1500 hour | Condition C, F50; ASTM D1693 |
| ESCR 10% Igepal? | >= 1500 hour | >= 1500 hour | Condition B, F50; ASTM D1693 |
| Melt Flow | 0.080 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.080 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C | 12 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2" (50mm) per min, Type IV; ASTM D638 |
| Elongation at Yield | 850 % | 850 % | Ultimate, 2" (50mm) per min, Type IV; ASTM D638 |
| Flexural Modulus | 0.827 GPa | 120 ksi | Tangent – 16:1 span:depth, 0.5 in./min.; ASTM D790 |
| Tensile Impact Strength | 504 kJ/m2 | 240 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | Method A; ASTM D648 |
| Vicat Softening Point | 243 °C | 469 °F | ASTM D648 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |