- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg, Temperature 190 °C | 20 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 21.4 MPa | 3100 psi | 2" (50mm) per min; ASTM D882 |
| Film Tensile Strength at Yield, TD | 21.4 MPa | 3100 psi | 2" (50mm) per min; ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | 2" (50mm) per min; ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | 2" (50mm) per min; ASTM D882 |
| Elmendorf Tear Strength MD | 50 g | 50 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 |
| Dart drop Test | 130 g @Thickness 660 mm | 0.287 lb @Thickness 26.0 in | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.1 MPa | 6100 psi | 2" (50mm) per min; ASTM D882 |
| Film Tensile Strength at Break, TD | 42.1 MPa | 6100 psi | 2" (50mm) per min; ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 4.0 | 4.0 | |