- 熔體流動速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.953
- 拉伸強度 [MPa]: 28.3
- 熱變形溫度 [℃]: 72.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 6.8 g/10 min | 6.8 g/10 min | ASTM D1238 |
| Spiral Flow | 24.1 cm | 9.50 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 22.4 MPa | 3250 psi | ASTM D638 |
| Tensile Strength, Yield | 28.3 MPa | 4110 psi | 2"/min; ASTM D638 |
| Elongation at Yield | 7.3 % | 7.3 % | 2"/min; ASTM D638 |
| 1% Secant Modulus | 1250 MPa | 181000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 1.04 GPa | 151 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |